The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis
(Elsevier Sci Ltd, Oxford, 2010)
BaTiO3 ceramic powders were prepared by a complex method based on the Pechini type reaction route and mechanically assisted synthesis. In both ways BaTiO3 ceramics were sintered after 120 min on 1300 degrees C without ...
Structure and photocatalytic properties of sintered TiO2 nanotube arrays
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Antimony doping effect on barium titanate structure and electrical properties
(Elsevier Sci Ltd, Oxford, 2011)
Nanopowders of pure and antimony doped barium titanate (BaTiO3-BT) were synthesized by polymeric precursors method based on Pechini process. Obtained powders were pressed and sintered at 1300 degrees C for 8 h. XRD analysis ...
Structural and electrical properties of sintered Fe2O3/TiO2 nanopowder mixtures
(Elsevier Sci Ltd, Oxford, 2014)
Starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) were mixed in the weight ratios 60:40 and 40:60. Green samples were sintered in the temperature range 750-1250 degrees C in air. Structural, morphological ...
Electrical Properties of Inkjet Printed Graphene Patterns on PET-Based Substrate
(IEEE Computer Society, 2015)
In this paper, electrical properties of inkjet printed graphene patterns on a PET-based (Novele (TM) IJ-220) substrate are presented. Water-soluble graphene conductive ink (Phene plus I3015) was used. Tested samples were ...
Synthesis of Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
Phase stability and electrochemical analysis of Nb doped BaCe 0.9Y0.1O3-x electrolyte for IT-SOFCs
(Electrochemical Society Inc., 2010)
Barium cerate-based electrolytes containing different amounts of Nb 5+ as a dopant were investigated with the aim of attaining materials with improved chemical stability. BaCe0.9.xNbxY 0.1O3-x (BCYN) powders with different ...
Influence of Nitrogen and Air Atmosphere During Thermal Treatment on Micro and Nano Sized Powders and Sintered TiO2 Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
Effect of preparation route on the microstructure and electrical conductivity of co-doped ceria
(Elsevier Sci Ltd, Oxford, 2013)
Dense Ce0.8Sm0.1Gd0.1O2-delta electrolytes were fabricated by sintering of CeO2 solid solutions which were prepared from metal nitrates and NaOH using self propagating room temperature synthesis (SPRT). Three different ...