Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Sintering and electrical properties of Ce1-xBixO2-delta solid solution
(Elsevier Science Sa, Lausanne, 2014)
Solid solution Ce1-xBixO2-delta nanopowders with the composition of x = 0.1-0.5 were synthesized by using Self Propagating Room Temperature procedure (SPRT). The results obtained by XRPD show that synthesized samples were ...
Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC
(Elsevier Science Sa, Lausanne, 2015)
A series of four different powders ceria doped Ce1-xErxO2-delta (0.05 lt = x lt = 0.20) were synthesized by applying self-propagating reaction at room temperature (SPRT method). SPRT procedure is based on the self-propagating ...
Nanostructured Fe2O3/TiO2 thick films: Analysis of structural and electronic properties
(Elsevier Sci Ltd, Oxford, 2015)
Thick films using starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) mixed in the weight ratios 60:40 and 40:60 for thick film paste were fabricated by screen printing technology on an alumina substrate. ...
Reheating of Zinc-titanate Sintered Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2015)
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during heating in nitrogen and air atmosphere. Interactions of bulk specimens with gaseous surrounding induce microstructure ...
Study on bi-layered ceramics powders prepared by the mechanochemical synthesis
(Elsevier Science Sa, Lausanne, 2009)
Bi-layered structured ferroelectric materials-bismuth titanate, Bi4Ti3O12 (BIT) and barium-bismuth titanate, BaBi4Ti4O15 (BBT) powders were prepared by homogenization and sintering of mixture of stehiometric quantities of ...
Change in structural, ferroelectric, and magnetic properties of bismuth ferrite induced by doping with gadolinium
(Elsevier Sci Ltd, Oxford, 2019)
Bismuth ferrite, BiFeO3, was doped with a wide range of concentrations (0-30%) of Gd in order to investigate structural, ferroelectric, and magnetic properties and their correlation. Powder samples of Bi1-xGdxFeO3 (x = ...
Dielectric and ferroelectric properties of BST ceramics obtained by a hydrothermally assisted complex polymerization method
(Elsevier Sci Ltd, Oxford, 2015)
Ba0.8Sr0.2TiO3 (BST) powder, obtained by a hydrothermal treatment of precursor solution previously prepared by a complex polymerization method (HT-CPM), was uniaxially pressed and sintered at 1280 degrees C for 1-32 h. The ...
Antiferromagnetism and heat capacity of NaCo2-xCuxO4 ceramics
(Elsevier Sci Ltd, Oxford, 2017)
Polycrystalline samples of NaCo2-xCuxO4 (x=0, 0.01, 0.03 and 0.05) were synthesized in two different ways: 1) by a mechanochemically assisted solid-state reaction method (MASSR) and 2) by a citric acid complex method (CAC). ...
The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis
(Elsevier Sci Ltd, Oxford, 2010)
BaTiO3 ceramic powders were prepared by a complex method based on the Pechini type reaction route and mechanically assisted synthesis. In both ways BaTiO3 ceramics were sintered after 120 min on 1300 degrees C without ...