Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes that will happen during subsequent heating. Powders were characterized with XRD, SEM and particle seizer. Subsequent heating was monitored on TGA/DTA in an air atmosphere. After compaction of the milled powders, sintering was also performed in a dilatometric device. Sintered specimens were characterized micro structurally with SEM on a fresh breakage. Obtained differential TGA diagrams suggest intensive changes during prolonged milling of the oxidation kinetics on heating. Ferrite powders changed with milling as well as with second run heating were characterized to enable determination of the potentially best ratio of milling and heating to be applied to obtain the desired microstructure.
Keywords:
Sintering / Milling / Ferrites / Dilatometry
Source:
Science of Sintering, 2017, 49, 4, 455-467
Publisher:
Međunarodni Institut za nauku o sinterovanju, Beograd
TY - JOUR
AU - Labus, Nebojša J.
AU - Vasiljević, Zorka Z
AU - Aleksić, Obrad
AU - Luković, Miloljub
AU - Marković, Smilja
AU - Pavlović, Vladimir B
AU - Mentus, Slavko
AU - Nikolić, Maria Vesna
PY - 2017
UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/1102
AB - Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes that will happen during subsequent heating. Powders were characterized with XRD, SEM and particle seizer. Subsequent heating was monitored on TGA/DTA in an air atmosphere. After compaction of the milled powders, sintering was also performed in a dilatometric device. Sintered specimens were characterized micro structurally with SEM on a fresh breakage. Obtained differential TGA diagrams suggest intensive changes during prolonged milling of the oxidation kinetics on heating. Ferrite powders changed with milling as well as with second run heating were characterized to enable determination of the potentially best ratio of milling and heating to be applied to obtain the desired microstructure.
PB - Međunarodni Institut za nauku o sinterovanju, Beograd
T2 - Science of Sintering
T1 - Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
EP - 467
IS - 4
SP - 455
VL - 49
DO - 10.2298/SOS1704455L
ER -
@article{
author = "Labus, Nebojša J. and Vasiljević, Zorka Z and Aleksić, Obrad and Luković, Miloljub and Marković, Smilja and Pavlović, Vladimir B and Mentus, Slavko and Nikolić, Maria Vesna",
year = "2017",
abstract = "Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes that will happen during subsequent heating. Powders were characterized with XRD, SEM and particle seizer. Subsequent heating was monitored on TGA/DTA in an air atmosphere. After compaction of the milled powders, sintering was also performed in a dilatometric device. Sintered specimens were characterized micro structurally with SEM on a fresh breakage. Obtained differential TGA diagrams suggest intensive changes during prolonged milling of the oxidation kinetics on heating. Ferrite powders changed with milling as well as with second run heating were characterized to enable determination of the potentially best ratio of milling and heating to be applied to obtain the desired microstructure.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment",
pages = "467-455",
number = "4",
volume = "49",
doi = "10.2298/SOS1704455L"
}
Labus, N. J., Vasiljević, Z. Z., Aleksić, O., Luković, M., Marković, S., Pavlović, V. B., Mentus, S.,& Nikolić, M. V.. (2017). Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 49(4), 455-467.
https://doi.org/10.2298/SOS1704455L
Labus NJ, Vasiljević ZZ, Aleksić O, Luković M, Marković S, Pavlović VB, Mentus S, Nikolić MV. Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment. in Science of Sintering. 2017;49(4):455-467.
doi:10.2298/SOS1704455L .
Labus, Nebojša J., Vasiljević, Zorka Z, Aleksić, Obrad, Luković, Miloljub, Marković, Smilja, Pavlović, Vladimir B, Mentus, Slavko, Nikolić, Maria Vesna, "Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment" in Science of Sintering, 49, no. 4 (2017):455-467,
https://doi.org/10.2298/SOS1704455L . .