High surface area Pd nanocatalyst on core-shell tungsten based support as a beneficial catalyst for low temperature fuel cells application
(Pergamon-Elsevier Science Ltd, Oxford, 2017)
Tungsten based support was prepared by polycondensation of resorcinol and formaldehyde from ammonium metatungstate, in the presence cetyltrimethylammonium bromide (CTABr) surfactant. Pd nanocatalyst on this support was ...
Synthesis and characterization of AgPd alloy coatings as beneficial catalysts for low temperature fuel cells application
(Pergamon-Elsevier Science Ltd, Oxford, 2019)
The Ag, Pd and AgPd alloys of different morphologies and compositions were electrodeposited onto Au and glassy carbon (GC) disc electrodes from the solution containing 0.001 M PdCl2 + 0.04 M AgCl + 0.1 M HCl + 12 M LiCl ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
Morphology and phase composition of as-deposited and recrystallized Ni-Mo-O powders
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The Ni-Mo-O alloy powders were electrodeposited from ammonium sulfate containing electrolytes for different Ni/Mo ions concentration ratios. Electrodeposition was investigated by the polarization measurements. The morphology, ...
Characterization of electrodeposited Cd-Co alloy coatings by anodic linear sweep voltammetry
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The electrodeposited Cd-Co alloys were characterized by the anodic linear sweep voltammetry (ALSV) technique in the solution of 1 M NaCl (pH 2). It is shown that Cd-Co alloys could be deposited with high current efficiency ...
Morphology and composition of the Fe-Ni powders electrodeposited from citrate containing electrolytes
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The electrodeposition of the Fe-Ni powders from citrate containing electrolytes for different Ni/Fe ions concentration ratios, using Fe(Ill) and Fe(II) salts at pH 4.5 and pH 4.0 respectively was investigated by the ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm(-3) NaOH, at 25 degrees C. Tungsten-carbide islands on nano-tungsten particles (WC) ...
RuOx nanoparticles deposited on TiO2 nanotube arrays by ion-exchange method as electrocatalysts for the hydrogen evolution reaction in acid solution
(Pergamon-Elsevier Science Ltd, Oxford, 2015)
Nanocomposite cathodes for the hydrogen evolution reaction (HER) were prepared by deposition of RuOx catalyst particles on self-organized titania nanotube (TiNT) arrays of highly developed surface area, following a procedure ...
Structural and electrical properties of BaCe(0.9)Ee(0.1)O(2.95) electrolyte for IT-SOFCs
(Pergamon-Elsevier Science Ltd, Oxford, 2015)
BaCe(0.9)Ee(0.1)O(2.95) (BCE) nanopowder was synthesized by citric-nitric autocombustion method. Rietveld refinement analysis showed that unit cell volume was slightly larger compared with the most known BaCe0.9Y0.1O2.95, ...