Grain Size and Porosity Dependence of Titanium Dioxide Nano-Paste on Sintering Temperature for Gas Sensing Application
(IEEE Computer Society, 2015)
If the material is being sintered, grain size of its particles will depend on the sintering temperature, time of the sintering and the pressure applied on the material while sintering. It is well known that on the lower ...
Application of Iron Manganite Thick Films for Humidity Sensing
(IEEE Computer Society, 2019)
Iron manganite (FeMnO3) thick film samples were obtained by screen printing four layers of thick film paste on alumina substrate with test PdAg electrodes. The paste was made by adding organic vehicles to iron manganite ...
Impedance Response of Pseudobrookite Thick Films with a Sandwich Configuration
(IEEE Computer Society, 2017)
We have investigated the impedance response of pseudobrookite thick films screen printed on alumina substrate in the temperature interval from room temperature to 350 degrees C in the frequency range 100 Hz - 1 MHz. Two ...
Application of Nanocrystalline Pseudobrookite (Fe2TiO5) Thick Films for Humidity Sensing
(IEEE Computer Society, 2018)
Pseudobrookite nanocrystalline thick films were screen printed on alumina substrate with small interdigitated PdAg electrodes (width 6 mm, length 12 mm, electrode spacing 0.2 mm) and fired at 600 degrees C for 30 minutes. ...
Pseudobrookite thick films for potential application as low-temperature sensitive material in NO gas sensors
(IEEE Computer Society, 2017)
Pseudobrookite thick films were obtained by screen printing paste composed of a 1: 1.5 molar ratio mixture of starting nanopowders of hematite and anatase, glass frit and organic binder. The films were deposited on alumina ...
Analysis of electronic properties of pseudobrookite thick films with possible application for NO gas sensing
(IEEE Computer Society, 2016)
Two pseudobrookite (PSB) containing pastes were composed of a mixture of starting nanopowders of hematite (alpha-Fe2O3) and anatase (TiO2) in the molar ratios 1: 1 (referred to as PSB-1) and 1:1.5 (referred to as PSB-1.5), ...