Influence of Synthesis Conditions on Morphological Features of the SBA-15 Containing Only Elongated and Rounded/Spherical Grains
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials ...
Solid State Synthesis of Extra Phase-Pure Li4Ti5O12 Spinel
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
Extra phase-pure Li4Ti5O12 spinel with particle sizes less than 500 nm was synthesized by solid state reaction of mechanochemicaly activated mixture of nano anatase and Li2CO3 for a very short annealing time, 4 h at 800 ...
Effect of Binder Molecular Weight on Morphology of TiO2 Films Prepared by Tape Casting and Their Photovoltaic Performance
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Titanium(IV) oxide in the form of anatase has proven to be the best choice for photoanodic material in dye-sensitized solar cells (DSCs). The aim of the work was to study the influence of binder molecular weight on the ...
Two Step Sintering of ZnTiO3 nanopowder
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were treated by conventional heating with isothermal holding at 931 degrees C for 10 minutes, 25 minutes and 40 minutes. ZnTiO3 compacts ...
Sixty years of the theory of B. Ya. Pines
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Electrical properties of ZnO varistors prepared by direct mixing of constituent phases
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Varistor samples containing different amounts of constituent phases were prepared by direct mixing of constituent phases. Detailed electrical characterization was performed to explain the influence of minor phases (spinel ...
Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...