Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature interval from room to 1380 degrees C with three different heating rates (10, 20 and 30 degrees C/min). Early-stage sintering mechanisms for all three types of samples were analyzed, showing significant differences between the non-activated and mechanically activated samples.
TY - JOUR
AU - Nikolić, Maria Vesna
AU - Pavlović, V. P.
AU - Pavlović, Vladimir B
AU - Ristic, M. M.
PY - 2006
UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/151
AB - Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature interval from room to 1380 degrees C with three different heating rates (10, 20 and 30 degrees C/min). Early-stage sintering mechanisms for all three types of samples were analyzed, showing significant differences between the non-activated and mechanically activated samples.
PB - Međunarodni Institut za nauku o sinterovanju, Beograd
T2 - Science of Sintering
T1 - Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
EP - 244
IS - 3
SP - 239
VL - 38
DO - 10.2298/SOS0603239N
ER -
@article{
author = "Nikolić, Maria Vesna and Pavlović, V. P. and Pavlović, Vladimir B and Ristic, M. M.",
year = "2006",
abstract = "Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature interval from room to 1380 degrees C with three different heating rates (10, 20 and 30 degrees C/min). Early-stage sintering mechanisms for all three types of samples were analyzed, showing significant differences between the non-activated and mechanically activated samples.",
publisher = "Međunarodni Institut za nauku o sinterovanju, Beograd",
journal = "Science of Sintering",
title = "Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3",
pages = "244-239",
number = "3",
volume = "38",
doi = "10.2298/SOS0603239N"
}
Nikolić, M. V., Pavlović, V. P., Pavlović, V. B.,& Ristic, M. M.. (2006). Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3. in Science of Sintering
Međunarodni Institut za nauku o sinterovanju, Beograd., 38(3), 239-244.
https://doi.org/10.2298/SOS0603239N
Nikolić MV, Pavlović VP, Pavlović VB, Ristic MM. Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3. in Science of Sintering. 2006;38(3):239-244.
doi:10.2298/SOS0603239N .
Nikolić, Maria Vesna, Pavlović, V. P., Pavlović, Vladimir B, Ristic, M. M., "Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3" in Science of Sintering, 38, no. 3 (2006):239-244,
https://doi.org/10.2298/SOS0603239N . .