Analysis of isothermal sintering of zinc-titanate doped with MgO
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Aerosol Deposition of Ba0.8Sr0.2TiO3 Thin Films
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2009)
In this work we optimized conditions for aerosol deposition of homogeneous, nano-grained, smooth Ba0.8Sr0.2TiO3 thin films. Investigation involved optimization of deposition parameters, namely deposition time and temperature ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
History and challenges of barium titanate: Part I
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
Barium titanate is the first ferroelectric ceramics and a good candidate for a variety of applications due to its excellent dielectric, ferroelectric and piezoelectric properties. Barium titanate is a member of a large ...
Intrinsic resistivity of sintered nickel manganite vs. powder activation time and density
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Thermal Diffusivity of Single Crystal Bi0.9Sb0.1
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2010)
A single crystal Bi0.9Sb0.1 ingot was synthesized using the Bridgman technique. Thermal diffusivity and electronic transport properties of single crystal cleaved plates (001) were determined from PA photoacoustic phase and ...
ZnTiO3 Ceramic Nanopowder Microstructure Changes During Compaction
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2013)
ZnTiO3 nanopowder as a constitutive component in compact production was primarily characterised. Scanning electron micrographs of as received powder were recorded. Mercury porosimetry and nitrogen adsorption were also ...
Influence of Nitrogen and Air Atmosphere During Thermal Treatment on Micro and Nano Sized Powders and Sintered TiO2 Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
History and Challenges of Barium Titanate: Part II
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
Barium titanate is the first ferroelectric ceramics and a good candidate for a variety of applications due to its excellent dielectric, ferroelectric and piezoelectric properties,. Barium titanate is a member of a large ...