Far infrared properties of sintered NiO
(Elsevier Sci Ltd, Oxford, 2007)
Far infrared reflection spectra of NiO polycrystals sintered at 1100 degrees C for various times (30-240 min) were measured at room temperature using a FTIR Spectrometer-Brucker 113V. The measured spectra depended on the ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Microstructural evolution and electric properties of mechanically activated BaTiO3 ceramics
(Elsevier Sci Ltd, Oxford, 2007)
Ceramic materials with a perovskite related structures such as non-doped and doped barium titanate ceramics are attracting much interest for their application as capacitor dielectrics, resistors, thermal sensors, etc. Since ...
Ispitivanje sinterovane cink-kalaj-oksidne keramike fotoakustičnom spektroskopijom / Photoacoustic spectroscopy investigation of sintered zinc-tin-oxide ceramics
(Savez hemijskih inženjera, Beograd, 2007)
Prahovi ZnO i SnO2 pomešani u molarnom odnosu 2:1 mehanički su aktivirani u planetarnim mlinu sa kuglama u intervalu od 10 do 160 minuta. Dobijene smeše presovane su i izotermski sinterovane na 1300 °C, dva sata. Uzorci ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Far infrared properties of sintered PbTe doped with boron
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fated using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm(-1) and 285 ...