Mesoporous films prepared from synthesized TiO2 nanoparticles and their application in dye-sensitized solar cells (DSSCs)
(Pergamon-Elsevier Science Ltd, Oxford, 2016)
In this paper, we propose a novel method for preparation of high surface area titania nanoparticles, and investigate their photovoltaic performance in dye sensitized solar cells (DSSCs). The precursor compound titanium(I ...
Kinetics of the hydrogen evolution reaction on Fe-Mo film deposited on mild steel support in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2005)
The mechanism and kinetics of the hydrogen evolution reaction were studied. in 1.0 mol dm(-3) NaOH solution on Fe-Mo alloy electrodes prepared by electrodeposition at constant current densities from a pyrophosphate bath. ...
Morphology and phase composition of as-deposited and recrystallized Ni-Mo-O powders
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The Ni-Mo-O alloy powders were electrodeposited from ammonium sulfate containing electrolytes for different Ni/Mo ions concentration ratios. Electrodeposition was investigated by the polarization measurements. The morphology, ...
Synthesis and characterization of MoOx-Pt/C and TiOx-Pt/C nano-catalysts for oxygen reduction
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The oxygen reduction reaction (ORR) was studied at carbon supported MoOx-Pt/C and TiOx-Pt nanocatalysts in 0.5 mol dm(-3) HClO4 solution, at 25 degrees C. The MoOx-Pt/C and TiOx-Pt/C catalysts were prepared by the polyole ...
Voltammetric and differential pulse determination of roxithromycin
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The oxidative behavior of antibiotic roxithromycin standard was studied at a gold electrode in 0.05 M NaHCO3 using cyclic linear sweep voltammetry and differential pulse voltammetry. It was found that the value of the ...
Morphology and composition of the Fe-Ni powders electrodeposited from citrate containing electrolytes
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The electrodeposition of the Fe-Ni powders from citrate containing electrolytes for different Ni/Fe ions concentration ratios, using Fe(Ill) and Fe(II) salts at pH 4.5 and pH 4.0 respectively was investigated by the ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm(-3) NaOH, at 25 degrees C. Tungsten-carbide islands on nano-tungsten particles (WC) ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
Characterization of electrodeposited Cd-Co alloy coatings by anodic linear sweep voltammetry
(Pergamon-Elsevier Science Ltd, Oxford, 2009)
The electrodeposited Cd-Co alloys were characterized by the anodic linear sweep voltammetry (ALSV) technique in the solution of 1 M NaCl (pH 2). It is shown that Cd-Co alloys could be deposited with high current efficiency ...
Service life test of non-noble metal composite cathodes for hydrogen evolution in sodium hydroxide solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
In this work polarization characteristics and "service life" test of the non-noble metal composite coatings Ni-MoOx and Ni-MoO2 for hydrogen evolution reaction (HER) in 32 wt.% NaOH at 90 degrees C were investigated and ...