Fast Oxide-Ion Conductors in Bi2O3-V2O5 System: Bi108-xVxO162+x(x=4-9) with 3 x 3 x 3 Superstructure
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2021)
In this study, the possibility to stabilize O-2 ion conductors in Bi2O3-V2O5 system was investigated. Six pseudo-binary Bi2O3-V2O5 mixtures [3.50 lt x(V2O5) lt 8.50 mol%] were thermally treated at 1000 degrees C for 1 ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Study of Barium Bismuth Titanate Prepared by Mechanochemical Synthesis
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2009)
Barium-bismuth titanate, BaBi4Ti4O15 (BBT), a member of Aurivillius bismuth-based layer-structure perovskites, was prepared from stoichiometric amounts of barium titanate and bismuth titanate obtained via mechanochemical ...
Far infrared properties of sintered PbTe doped with boron
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fated using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm(-1) and 285 ...
Characterization of Sedimentary Minerals from Kolubara Mining Basin, Serbia, with the Determination of Natural Radioactivity
(International Institute for the Science of Sintering, 2022)
Diatomite (diatomaceous earth) and clay minerals deposits from the mining basin Kolubara, Serbia, are natural materials with high economic potential in many fields. As received and treated materials, diatomite and clay ...
Synthesis of Anatase Nanopowders by Sol-gel Method and Influence of Temperatures of Calcination to Their Photocatalitic Properties
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2015)
The titanium dioxide (TiO2) nanopowders were produced by sol-gel technique from tetrabutyl titanate as a precursor, varying the temperature of calcination (from 500 to 550 degrees C with the step of 10 degrees C). XRPD ...
Two Step Sintering of ZnTiO3 nanopowder
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were treated by conventional heating with isothermal holding at 931 degrees C for 10 minutes, 25 minutes and 40 minutes. ZnTiO3 compacts ...
Sixty years of the theory of B. Ya. Pines
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Sol-gel Synthesis of Anatase Nanopowders for Efficient Photocatalytic Degradation of Herbicide Clomazone in Aqueous Media
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
TiO2 nanopowders were produced by sol-gel technique using TiCl4 as a starting material. For the preparation of crystalline anatase with developed surface area, this aqueous solution has been mixed with 0.05 M or 0.07 M ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...