Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
Synthesis of BaTiO3 from a mechanically activated BaCO3-TiO2 system
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
Far infrared properties of sintered PbTe doped with boron
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Far infrared spectra of sintered PbTe doped with boron were analyzed. The measured infrared spectra were fated using a modified plasmon-phonnon interaction model with two additional oscillators (at about 195 cm(-1) and 285 ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Effect of Milling Time on Mechanical Properties of Anorthite Obtained by Thermal Transformation of Ca-LTA Zeolite
(International Institute for the Science of Sintering, 2022)
Anorthite ceramics was fabricated from calcium exchanged Na-LTA zeolite. The powder compacts of Ca-LTA zeolite were sintered at different temperatures ranging between 1100 and 1400°C. It was found that the temperature of ...