Far infrared properties of sintered NiO
(Elsevier Sci Ltd, Oxford, 2007)
Far infrared reflection spectra of NiO polycrystals sintered at 1100 degrees C for various times (30-240 min) were measured at room temperature using a FTIR Spectrometer-Brucker 113V. The measured spectra depended on the ...
Tailoring of morphology and orientation of LaNiO3 films from polymeric precursors
(Elsevier Sci Ltd, Oxford, 2007)
The aim of this work was to prepare lanthanum nickel oxide (LaNiO3, LNO) thin films of different morphology and orientation. The precursor solutions were prepared by a chemical method from citric salts of lanthanum and ...
Screen printed PLZT thick films prepared from nanopowders
(Elsevier Sci Ltd, Oxford, 2007)
The gap between the bulk materials and thin films can be filled with thick films suitably designed and appropriate processed. Thick films of complex system like lead-lanthanum-zirconium titanate (PLZT) is difficult to ...
Spectroscopic study of spinel ZnCr2O4 obtained from mechanically activated ZnO-Cr2O3 mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and Cr2O3 powders in equimolar quantities was mechanically activated by grinding using a high energy vibro-mil I for 0, 40 and 80 min. The spinet ZnCr2O4 was prepared from activated mixtures by a ...
Phase evolution in Ce-doped yttrium-aluminum-based particles derived from aerosol
(Elsevier Sci Ltd, Oxford, 2007)
The common nitrates precursor solution leading to the Y3Al5O12:Ce3+ (YAG:Ce) composition with 2 at.% of cerium, is ultrasonically atomised and introduced into the tubular flow reactor at 320 degrees C. Having in mind that ...
Investigation on possibility of mechanochemical synthesis of CaTiO3 from different precursors
(Elsevier Sci Ltd, Oxford, 2007)
Recently, mechanochemical synthesis was widely used in preparation of perovskite type of materials, such as BaTiO3, PbTiO3, PZT, etc. In this work, the possibility of mechanochemical synthesis of CaTiO3 from different ...
ZnO varistors from intensively milled powders
(Elsevier Sci Ltd, Oxford, 2007)
Two ways of application of intensive milling in ZnO varistors processing were compared. First was intensive milling of mixture of previously prepared constituent phases. In this case, intensive milling was applied only to ...
ZnO varistors with reduced amount of additives prepared by direct mixing of constituent phases
(Elsevier Sci Ltd, Oxford, 2007)
The aim of this work was to reduce number of additives using new method of preparation, refered as "direct mixing of the constituent phases". The method is based on sintering of a mixture of constituent phases with the ...
Optimization of processing parameters for preparation of LaNiO3 thin films from the citrate precursors
(Elsevier Sci Ltd, Oxford, 2007)
Lanthanum nickel oxide (LaNiO3) is an electrically conductive ceramics, which has a potential use as electrode for ferroelectric thin films, multilayer actuators and many other electronic devices. In this work, LaNiO3 thin ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...