Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Microstructural characterization of mechanically activated ZnO-Cr2O3 system
(Elsevier Sci Ltd, Oxford, 2005)
An equimolar mixtures of starting ZnO and Cr2O3 powders were mechanically activated by grinding using a planetary ball mill for various periods of time (40-320min). Formation of nanocrystalline ZnCr2O4 as normal spine] ...
The nature of structural changes in nanocrystalline ZnO powders under linear heating conditions
(Elsevier Sci Ltd, Oxford, 2004)
The nature of exothermal and irreversible structural changes observed during linear heating of nanocrystalline ZnO powders was investigated using differential scanning calorimetry, X ray, SEM and TEM analysis. Nanocrystalline ...
Preparation of nanostructured Zn-Cr-O spinel powders by ultrasonic spray pyrolysis
(Elsevier Sci Ltd, Oxford, 2001)
Ultrasonic spray pyrolysis (1.7 MHz) has been applied for the generation of zinc chromium oxide submicronic (470 nm) particles from the corresponding metal nitrate solution. Heterogeneous gas-liquid/solid chemical reactions ...