Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Structural analysis of Zn2TiO4 doped with mgo
(Springer New York LLC, 2009)
The starting mixtures of ZnO, TiO2, and MgO (0, 1.25, and 2.5 wt.%) powders are mechanically activated in a high-energy planetary mill for 15 min and then sintered between 800 and 1100 degrees C for 2 h. The influence of ...
Modification of the structural and optical properties of commercial ZnO powder by mechanical activation
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy ...
Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...
The influence of mechanical activation on the stoichiometry and defect structure of a sintered ZnO-Cr2O3 system
(Trans Tech Publications Ltd, 2004)
Mixtures of starting ZnO and Cr2O3 powders in equimolar quantities were mechanically activated by grinding using a high energy vibro-mill for 0, 40 and 80 minutes. Qualitative X-ray diffraction analysis made after sintering ...