Properties of lanthanum doped BaTiO3 produced from nanopowders
(Elsevier Sci Ltd, Oxford, 2010)
Pure and barium titanate (BT) powders doped with different lanthanum concentration were prepared by the polymeric precursor method (Pechini process) which was carried out as a three-stage process from organometallic ...
Penetration depth of electron-doped infinite-layer Sr0.88La0.12CuO2+x thin films
(Amer Physical Soc, College Pk, 2010)
The in-plane penetration depth of Sr0.88La0.12CuO2+x thin films at various doping obtained from oxygen reduction has been measured, using ac-susceptibility measurements. For the higher doping samples, the superfluid density ...
Dielectric and relaxor behavior of BaBi4Ti4O15 ceramics
(Elsevier Science Sa, Lausanne, 2010)
Barium bismuth titanate BaBi4Ti4O15 (BBiT) ceramics have been prepared using non-conventional solid-state reaction route based on mechanochemical synthesis during intensive milling. The X-ray diffraction method was used ...
The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis
(Elsevier Sci Ltd, Oxford, 2010)
BaTiO3 ceramic powders were prepared by a complex method based on the Pechini type reaction route and mechanically assisted synthesis. In both ways BaTiO3 ceramics were sintered after 120 min on 1300 degrees C without ...
Properties of MnZn ferrites prepared by powder injection molding technology
(Elsevier Science Bv, Amsterdam, 2010)
In this work, manganese zinc ferrite components were manufactured by powder injection molding-PIM technology. A fine powder consisting of Mn1-xZnxFe2O4 with small addition of hematite alpha-Fe2O3 as used in mass ferrite ...
The effect of the electrode surface roughness at low level of coarseness on the polarization characteristics of electrochemical processes
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
In this study, it is considered: (a) the effect of the exchange current density to the limiting diffusion current density ratio (J(0)/J(L)) at low level of surface coarseness on the polarization characteristics of the ...
Application of pulsating overpotential regime on the formation of copper deposits in the range of hydrogen co-deposition
(Springer, New York, 2010)
Electrodeposition of copper by pulsating overpotential (PO) regime in the range of hydrogen co-deposition was examined by scanning electron microscopy. It was found that the increase of the pause-to-pulse ratio produced a ...