Microstructural investigation of the PZT films prepared from the suspension of nanocrystalline powders
(Elsevier Sci Ltd, Oxford, 2004)
PZT thin films of composition Pb(Zr0.52Ti0.48)O-3 were prepared by a novel method from the suspension of nanocrystalline PZT powders. The powders were obtained by mechanochemical synthesis. Films were deposited on silicon ...
Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions
(Elsevier Sci Ltd, Oxford, 2005)
SnO2 varistors doped with CoO, Cr2O3 and Nb2O5 were prepared by evaporation and decomposition of suspensions. The composition of the varistors was optimized to improve electrical properties, such as nonlinearity, leakage ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
ZnO varistors from intensively milled powders
(Elsevier Sci Ltd, Oxford, 2007)
Two ways of application of intensive milling in ZnO varistors processing were compared. First was intensive milling of mixture of previously prepared constituent phases. In this case, intensive milling was applied only to ...
The nature of structural changes in nanocrystalline ZnO powders under linear heating conditions
(Elsevier Sci Ltd, Oxford, 2004)
The nature of exothermal and irreversible structural changes observed during linear heating of nanocrystalline ZnO powders was investigated using differential scanning calorimetry, X ray, SEM and TEM analysis. Nanocrystalline ...
Preparation of nanostructured Zn-Cr-O spinel powders by ultrasonic spray pyrolysis
(Elsevier Sci Ltd, Oxford, 2001)
Ultrasonic spray pyrolysis (1.7 MHz) has been applied for the generation of zinc chromium oxide submicronic (470 nm) particles from the corresponding metal nitrate solution. Heterogeneous gas-liquid/solid chemical reactions ...
Microstructural characterization of mechanically activated ZnO-Cr2O3 system
(Elsevier Sci Ltd, Oxford, 2005)
An equimolar mixtures of starting ZnO and Cr2O3 powders were mechanically activated by grinding using a planetary ball mill for various periods of time (40-320min). Formation of nanocrystalline ZnCr2O4 as normal spine] ...