Structure study of nanosized La- and Sb-doped BaTiO3
(Elsevier Science Sa, Lausanne, 2010)
Lanthanum and antimony doped barium titanate powders were prepared by polymeric precursors method through Pechini process. Obtained powder was pressed into pellet and sintering was performed at 1300 degrees C for 8 h. The ...
Magnetic properties of doped LaMnO3 ceramics obtained by a polymerizable complex method
(Springer, Dordrecht, 2010)
Substituted lanthanum manganites with the general formula A(1-x) B (x) MnO3 (A = La, B = Ca, SraEuro broken vertical bar) have attracted a lot of attention due to their exceptional electric and magnetic properties. In this ...
Sintering and electrical properties of Ce1-xBixO2-delta solid solution
(Elsevier Science Sa, Lausanne, 2014)
Solid solution Ce1-xBixO2-delta nanopowders with the composition of x = 0.1-0.5 were synthesized by using Self Propagating Room Temperature procedure (SPRT). The results obtained by XRPD show that synthesized samples were ...
Dielectric and ferroelectric properties of BST ceramics obtained by a hydrothermally assisted complex polymerization method
(Elsevier Sci Ltd, Oxford, 2015)
Ba0.8Sr0.2TiO3 (BST) powder, obtained by a hydrothermal treatment of precursor solution previously prepared by a complex polymerization method (HT-CPM), was uniaxially pressed and sintered at 1280 degrees C for 1-32 h. The ...
Antiferromagnetism and heat capacity of NaCo2-xCuxO4 ceramics
(Elsevier Sci Ltd, Oxford, 2017)
Polycrystalline samples of NaCo2-xCuxO4 (x=0, 0.01, 0.03 and 0.05) were synthesized in two different ways: 1) by a mechanochemically assisted solid-state reaction method (MASSR) and 2) by a citric acid complex method (CAC). ...
Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC
(Elsevier Science Sa, Lausanne, 2015)
A series of four different powders ceria doped Ce1-xErxO2-delta (0.05 lt = x lt = 0.20) were synthesized by applying self-propagating reaction at room temperature (SPRT method). SPRT procedure is based on the self-propagating ...
Reheating of Zinc-titanate Sintered Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2015)
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during heating in nitrogen and air atmosphere. Interactions of bulk specimens with gaseous surrounding induce microstructure ...
The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis
(Elsevier Sci Ltd, Oxford, 2010)
BaTiO3 ceramic powders were prepared by a complex method based on the Pechini type reaction route and mechanically assisted synthesis. In both ways BaTiO3 ceramics were sintered after 120 min on 1300 degrees C without ...
Structure and photocatalytic properties of sintered TiO2 nanotube arrays
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...