Electrical properties of ZnO varistors prepared by direct mixing of constituent phases
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Varistor samples containing different amounts of constituent phases were prepared by direct mixing of constituent phases. Detailed electrical characterization was performed to explain the influence of minor phases (spinel ...
History and challenges of barium titanate: Part I
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
Barium titanate is the first ferroelectric ceramics and a good candidate for a variety of applications due to its excellent dielectric, ferroelectric and piezoelectric properties. Barium titanate is a member of a large ...
Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Analysis of isothermal sintering of zinc-titanate doped with MgO
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, TiO2 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes ...
A phenomenological analysis of sintering kinetics from the viewpoint of activated volume
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2005)
The sintering kinetics of real systems has been viewed as a process of transport of activated volume. Activated volume is a parameter that can be used to describe mass transport during the sintering process. It defines the ...
Electrical Characterization and Impedance Response of Lanthanum Doped Barium Titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
The dielectric permittivity and dissipation factor of La-doped and undoped BaTiO3 were investigated as a function of frequency and temperature. The impedance response was used to study the electrical properties of La-doped ...
Influence of Bi2O3 on microstructure and electrical properties of ZnO-SnO2 ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
The effects of small amounts (0.5; 1.0 and 1.5 mol. %) of bismuth oxide on the microstructure and electrical properties of ZnO-SnO2 ceramics have been studied. Starting powders of ZnO and SnO2 were mixed in the molar ratio ...
Synthesis of BaTiO3 from a mechanically activated BaCO3-TiO2 system
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
History and Challenges of Barium Titanate: Part II
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
Barium titanate is the first ferroelectric ceramics and a good candidate for a variety of applications due to its excellent dielectric, ferroelectric and piezoelectric properties,. Barium titanate is a member of a large ...
Intrinsic resistivity of sintered nickel manganite vs. powder activation time and density
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...