Magnetic properties of doped LaMnO3 ceramics obtained by a polymerizable complex method
(Springer, Dordrecht, 2010)
Substituted lanthanum manganites with the general formula A(1-x) B (x) MnO3 (A = La, B = Ca, SraEuro broken vertical bar) have attracted a lot of attention due to their exceptional electric and magnetic properties. In this ...
Influence of Nitrogen and Air Atmosphere During Thermal Treatment on Micro and Nano Sized Powders and Sintered TiO2 Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
Effect of preparation route on the microstructure and electrical conductivity of co-doped ceria
(Elsevier Sci Ltd, Oxford, 2013)
Dense Ce0.8Sm0.1Gd0.1O2-delta electrolytes were fabricated by sintering of CeO2 solid solutions which were prepared from metal nitrates and NaOH using self propagating room temperature synthesis (SPRT). Three different ...
Synthesis of Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
Structure study of nanosized La- and Sb-doped BaTiO3
(Elsevier Science Sa, Lausanne, 2010)
Lanthanum and antimony doped barium titanate powders were prepared by polymeric precursors method through Pechini process. Obtained powder was pressed into pellet and sintering was performed at 1300 degrees C for 8 h. The ...
Analysis and Modeling of Sintering of Sr-hexaferrite Produced by PIM Technology
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
The powder injection moulding (PIM) technology is lately becoming more and more significant due to complex design possibilities and good repeatability. This technology requires optimization of all steps starting with ...
Phase stability and electrochemical analysis of Nb doped BaCe 0.9Y0.1O3-x electrolyte for IT-SOFCs
(Electrochemical Society Inc., 2010)
Barium cerate-based electrolytes containing different amounts of Nb 5+ as a dopant were investigated with the aim of attaining materials with improved chemical stability. BaCe0.9.xNbxY 0.1O3-x (BCYN) powders with different ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Sintering and electrical properties of Ce1-xBixO2-delta solid solution
(Elsevier Science Sa, Lausanne, 2014)
Solid solution Ce1-xBixO2-delta nanopowders with the composition of x = 0.1-0.5 were synthesized by using Self Propagating Room Temperature procedure (SPRT). The results obtained by XRPD show that synthesized samples were ...
Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC
(Elsevier Science Sa, Lausanne, 2015)
A series of four different powders ceria doped Ce1-xErxO2-delta (0.05 lt = x lt = 0.20) were synthesized by applying self-propagating reaction at room temperature (SPRT method). SPRT procedure is based on the self-propagating ...