Influence of Synthesis Conditions on Morphological Features of the SBA-15 Containing Only Elongated and Rounded/Spherical Grains
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
Mesoporous silica SBA-15 materials of high specific surface area (similar to 700 m(2) g(-1)) were synthesized by using block copolymer Pluronic P123 as template and tetraethoxysilane as silica source. The obtained materials ...
Reheating of Zinc-titanate Sintered Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2015)
The scope of this work was observing dimensional and heat transfer changes in ZnTiO3 samples during heating in nitrogen and air atmosphere. Interactions of bulk specimens with gaseous surrounding induce microstructure ...
Effect of Binder Molecular Weight on Morphology of TiO2 Films Prepared by Tape Casting and Their Photovoltaic Performance
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Titanium(IV) oxide in the form of anatase has proven to be the best choice for photoanodic material in dye-sensitized solar cells (DSCs). The aim of the work was to study the influence of binder molecular weight on the ...
Synthesis of Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
Influence of Nitrogen and Air Atmosphere During Thermal Treatment on Micro and Nano Sized Powders and Sintered TiO2 Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
SiC Synthesis Using Natural Mg-Silicates
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
The silicon carbide powders are prepared by carbothermal reduction of domestic mineral resources (white and brown sepiolite), at relatively low temperatures (1200 - 1600 degrees C). Carbothermal reduction process is greatly ...
Analysis and Modeling of Sintering of Sr-hexaferrite Produced by PIM Technology
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
The powder injection moulding (PIM) technology is lately becoming more and more significant due to complex design possibilities and good repeatability. This technology requires optimization of all steps starting with ...
Thermal Diffusivity of Single Crystal Bi0.9Sb0.1
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2010)
A single crystal Bi0.9Sb0.1 ingot was synthesized using the Bridgman technique. Thermal diffusivity and electronic transport properties of single crystal cleaved plates (001) were determined from PA photoacoustic phase and ...
Solid State Synthesis of Extra Phase-Pure Li4Ti5O12 Spinel
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
Extra phase-pure Li4Ti5O12 spinel with particle sizes less than 500 nm was synthesized by solid state reaction of mechanochemicaly activated mixture of nano anatase and Li2CO3 for a very short annealing time, 4 h at 800 ...
ZnTiO3 Ceramic Nanopowder Microstructure Changes During Compaction
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2013)
ZnTiO3 nanopowder as a constitutive component in compact production was primarily characterised. Scanning electron micrographs of as received powder were recorded. Mercury porosimetry and nitrogen adsorption were also ...