Dielectric and magnetic properties of BaTiO3-NiFe2O4 multiferroic composites
(Elsevier Sci Ltd, Oxford, 2014)
Multiferroic composites with the general formula x BaTiO3-(1-x) NiFe2O4 (x=0.5, 0.7, 0.8) were prepared by mixing chemically obtained nickel ferrite and barium titanate powders. Optimum processing parameters for a reduction ...
Preparation, sintering and electrical properties of nano-grained multidoped ceria
(Elsevier Sci Ltd, Oxford, 2010)
Multiply doped ceria nanopowders were synthesized by applying MGNP (modified glycine/nitrate procedure). The overall concentration of dopants was kept constant (x = 0.2) whereby Gd ion as the main dopant was gradually ...
Comparative study of CeO2 nanopowders obtained by the hydrothermal method from various precursors
(Elsevier Sci Ltd, Oxford, 2015)
The effects of common precursors used in the synthesis of CeO2 nanopowders were investigated, and the structural and spectral properties of the resulting products were compared. Two cerium (III) salts, i.e., Ce(NO3)(3)center ...
Improvement of barium titanate properties induced by attrition milling
(Elsevier Sci Ltd, Oxford, 2012)
Barium titanate powder was prepared by soft chemical process from polymeric precursors (modified Pechini process). The synthesized barium titanate (BT) powder was nanosized and the factor of agglomeration (F-agg) pointed ...
Influence of mechanical activation on sphene based ceramic material synthesis
(Elsevier Sci Ltd, Oxford, 2013)
Sphene (CaTiSiO5), a calcium titanosilicate ceramic has been prepared from a powder mixture of CaCO3, TiO2 and SiO2 using vibromilling for homogenization and activation of precursors. The mechanochemical process initially ...
High-voltage electrophoretic deposition of preferentially oriented films from multiferroic YMn2O5 nanopowders
(Elsevier Sci Ltd, Oxford, 2013)
Processing of the YMn2O5 powder is very challenging, since it decomposes to YMnO3 and Mn3O4 at temperatures close to 1180 degrees C, while samples consolidation commonly demands high temperatures. The main goal of this ...
Physical-mechanical and microstructural properties of alkali-activated fly ash-blast furnace slag blends
(Elsevier Sci Ltd, Oxford, 2015)
This paper investigated physical mechanical and microstructural properties of alkali-activated binders based on blends of fly ash (FA) and blast furnace slag (BFS). FA BFS blends were alkali-activated with sodium silicate ...
Dielectric and ferroelectric properties of BST ceramics obtained by a hydrothermally assisted complex polymerization method
(Elsevier Sci Ltd, Oxford, 2015)
Ba0.8Sr0.2TiO3 (BST) powder, obtained by a hydrothermal treatment of precursor solution previously prepared by a complex polymerization method (HT-CPM), was uniaxially pressed and sintered at 1280 degrees C for 1-32 h. The ...
Structural, electrical and magnetic properties of nickel manganite obtained by a complex polymerization method
(Elsevier Sci Ltd, Oxford, 2014)
Structural, electrical and magnetic properties of nickel manganite ceramics obtained by sintering fine powders prepared by a complex polymerization method are given in this work. The phase composition of the synthesized ...
Ex-situ sensitization of ordered TiO2 nanotubes with CdS quantum dots
(Elsevier Sci Ltd, Oxford, 2015)
Ordered titania nanotubes (pore diameter approximate to 90 nm and wall thickness approximate to 10 nm) were obtained by the anodization technique and used for the ex-situ deposition of cadmium sulfide quantum dots (CdS ...