The influence of tribophysical activation on non-isothermal sintering of BaTiO3 ceramics
(Trans Tech Publications Ltd, Durnten-Zurich, 2006)
In this paper the influence of tribophysical activation on non-isothermal sintering of barium titanate has been investigated. BaTiO3 Powders were tribophysically activated in a planetary ball mill for 0, 60 and 120 min., ...
Photoacoustic and optical properties of zinc-stannate thin films
(Trans Tech Publications Ltd, Durnten-Zurich, 2006)
Thin films of single-phase zinc-stannate (Zn2SnO4) were grown by rf magnetron sputtering onto glass substrates. Transmission in the visible range was measured allowing determination of the energy gap and thickness of ...
In vitro multiplication of willow gentian (Gentiana asclepiadea L.) and the production of gentiopicrine and mangiferin
(Phyton - Annales Rei Botanicae, 2006)
A protocol for in vitro propagation of Gentiana asclepiadea was developed. The best multiplication rate was obtained with woody plant medium (WPM) supplemented with 8.9 mu M BAP (6-benzylaminopurine) and 1.1 mu M IAA ...
Electrical properties of ZnO varistors prepared by direct mixing of constituent phases
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Varistor samples containing different amounts of constituent phases were prepared by direct mixing of constituent phases. Detailed electrical characterization was performed to explain the influence of minor phases (spinel ...
Infrared properties of sintered alpha-MnSe
(Carl Hanser Verlag, Munich, 2006)
Far-infrared reflection spectra of sintered alpha-MnSe were measured at room temperature. The measured spectrum had one pronounced peak in accordance with literature data and group theory estimation and one smaller peak ...
Electrical characterization of the grain-boundary region of SnO2 varistors
(Trans Tech Publications Ltd, 2006)
The effect of Co, Cr and Nb on the electrical properties of the grain boundaries of SnO2-based varistors was investigated. The powders were prepared by the method of evaporation and decomposition of solutions and suspensions. ...
Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...
Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Modification of the structural and optical properties of commercial ZnO powder by mechanical activation
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy ...
Sixty years of the theory of B. Ya. Pines
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)