Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...
Far infrared reflectance of sintered Zn2TiO4
(Springer, New York, 2008)
Zinc-titanate ceramics were obtained by initial mechanical activation in a high-energy planetary mill for 15 min followed by sintering at temperatures 900-1100 degrees C for 2 h. Room temperature far infrared reflectivity ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Structural analysis of Zn2TiO4 doped with mgo
(Springer New York LLC, 2009)
The starting mixtures of ZnO, TiO2, and MgO (0, 1.25, and 2.5 wt.%) powders are mechanically activated in a high-energy planetary mill for 15 min and then sintered between 800 and 1100 degrees C for 2 h. The influence of ...
Intrinsic resistivity of sintered nickel manganite vs. powder activation time and density
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Synthesis of BaTiO3 from a mechanically activated BaCO3-TiO2 system
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
Ispitivanje sinterovane cink-kalaj-oksidne keramike fotoakustičnom spektroskopijom / Photoacoustic spectroscopy investigation of sintered zinc-tin-oxide ceramics
(Savez hemijskih inženjera, Beograd, 2007)
Prahovi ZnO i SnO2 pomešani u molarnom odnosu 2:1 mehanički su aktivirani u planetarnim mlinu sa kuglama u intervalu od 10 do 160 minuta. Dobijene smeše presovane su i izotermski sinterovane na 1300 °C, dva sata. Uzorci ...
Modification of the structural and optical properties of commercial ZnO powder by mechanical activation
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy ...
The influence of mechanical activation on the stoichiometry and defect structure of a sintered ZnO-Cr2O3 system
(Trans Tech Publications Ltd, 2004)
Mixtures of starting ZnO and Cr2O3 powders in equimolar quantities were mechanically activated by grinding using a high energy vibro-mill for 0, 40 and 80 minutes. Qualitative X-ray diffraction analysis made after sintering ...