Synthesis of Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
Dielectric and ferroelectric properties of BST ceramics obtained by a hydrothermally assisted complex polymerization method
(Elsevier Sci Ltd, Oxford, 2015)
Ba0.8Sr0.2TiO3 (BST) powder, obtained by a hydrothermal treatment of precursor solution previously prepared by a complex polymerization method (HT-CPM), was uniaxially pressed and sintered at 1280 degrees C for 1-32 h. The ...
Antiferromagnetism and heat capacity of NaCo2-xCuxO4 ceramics
(Elsevier Sci Ltd, Oxford, 2017)
Polycrystalline samples of NaCo2-xCuxO4 (x=0, 0.01, 0.03 and 0.05) were synthesized in two different ways: 1) by a mechanochemically assisted solid-state reaction method (MASSR) and 2) by a citric acid complex method (CAC). ...
Structure and photocatalytic properties of sintered TiO2 nanotube arrays
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2018)
One-dimensional (1D) TiO2 nanotubes perpendicular to the substrate were obtained by electrochemical oxidation of titanium foil in an acid electrolyte. In order to alter the crystallinity and the morphology of films the ...
Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Antimony doping effect on barium titanate structure and electrical properties
(Elsevier Sci Ltd, Oxford, 2011)
Nanopowders of pure and antimony doped barium titanate (BaTiO3-BT) were synthesized by polymeric precursors method based on Pechini process. Obtained powders were pressed and sintered at 1300 degrees C for 8 h. XRD analysis ...
Structural and electrical properties of sintered Fe2O3/TiO2 nanopowder mixtures
(Elsevier Sci Ltd, Oxford, 2014)
Starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) were mixed in the weight ratios 60:40 and 40:60. Green samples were sintered in the temperature range 750-1250 degrees C in air. Structural, morphological ...
Electrical Properties of Inkjet Printed Graphene Patterns on PET-Based Substrate
(IEEE Computer Society, 2015)
In this paper, electrical properties of inkjet printed graphene patterns on a PET-based (Novele (TM) IJ-220) substrate are presented. Water-soluble graphene conductive ink (Phene plus I3015) was used. Tested samples were ...
Change in structural, ferroelectric, and magnetic properties of bismuth ferrite induced by doping with gadolinium
(Elsevier Sci Ltd, Oxford, 2019)
Bismuth ferrite, BiFeO3, was doped with a wide range of concentrations (0-30%) of Gd in order to investigate structural, ferroelectric, and magnetic properties and their correlation. Powder samples of Bi1-xGdxFeO3 (x = ...
Nanostructured Fe2O3/TiO2 thick films: Analysis of structural and electronic properties
(Elsevier Sci Ltd, Oxford, 2015)
Thick films using starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) mixed in the weight ratios 60:40 and 40:60 for thick film paste were fabricated by screen printing technology on an alumina substrate. ...