ZnTiO3 Ceramic Nanopowder Microstructure Changes During Compaction
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2013)
ZnTiO3 nanopowder as a constitutive component in compact production was primarily characterised. Scanning electron micrographs of as received powder were recorded. Mercury porosimetry and nitrogen adsorption were also ...
Synthesis of Barium-zinc-titanate Ceramics
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Mixtures of BaCO3, ZnO and TiO2 powders, with molar ratio of 1:2:4, were mechanically activated for 20, 40 and minutes in a planetary ball mill. The resulting powders were compacted into pellets and isothermally sintered ...
Influence of Nitrogen and Air Atmosphere During Thermal Treatment on Micro and Nano Sized Powders and Sintered TiO2 Specimens
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2014)
The influence of air and nitrogen atmosphere during heating on TiO2 nano and micro sized powders as well as sintered polycrystalline specimens was analyzed. Sintering of TiO2 nano and micro powders in air atmosphere was ...
Thermal Diffusivity of Single Crystal Bi0.9Sb0.1
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2010)
A single crystal Bi0.9Sb0.1 ingot was synthesized using the Bridgman technique. Thermal diffusivity and electronic transport properties of single crystal cleaved plates (001) were determined from PA photoacoustic phase and ...
Solid State Synthesis of Extra Phase-Pure Li4Ti5O12 Spinel
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
Extra phase-pure Li4Ti5O12 spinel with particle sizes less than 500 nm was synthesized by solid state reaction of mechanochemicaly activated mixture of nano anatase and Li2CO3 for a very short annealing time, 4 h at 800 ...
Analysis and Modeling of Sintering of Sr-hexaferrite Produced by PIM Technology
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2011)
The powder injection moulding (PIM) technology is lately becoming more and more significant due to complex design possibilities and good repeatability. This technology requires optimization of all steps starting with ...
SiC Synthesis Using Natural Mg-Silicates
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
The silicon carbide powders are prepared by carbothermal reduction of domestic mineral resources (white and brown sepiolite), at relatively low temperatures (1200 - 1600 degrees C). Carbothermal reduction process is greatly ...
Effect of Binder Molecular Weight on Morphology of TiO2 Films Prepared by Tape Casting and Their Photovoltaic Performance
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2012)
Titanium(IV) oxide in the form of anatase has proven to be the best choice for photoanodic material in dye-sensitized solar cells (DSCs). The aim of the work was to study the influence of binder molecular weight on the ...
Synthesis of Anatase Nanopowders by Sol-gel Method and Influence of Temperatures of Calcination to Their Photocatalitic Properties
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2015)
The titanium dioxide (TiO2) nanopowders were produced by sol-gel technique from tetrabutyl titanate as a precursor, varying the temperature of calcination (from 500 to 550 degrees C with the step of 10 degrees C). XRPD ...
Structural and Electrical Properties of Ti Doped alpha-Fe2O3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2013)
In this work we have analyzed the effects of Ti doping on structural and electrical properties of alpha-Fe2O3. When the amount of added Ti (5 wt.% TiO2) was within the solubility degree and XRD, SEM and EDS analysis revealed ...