Effect of chemisorbed CO on MoOx-Pt/C electrode on the kinetics of hydrogen oxidation reaction
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The influence of poisoning of MoOx-Pt catalyst by CO on the kinetics of H-2 oxidation reaction (HOR) at MoOx-Pt electrode in 0 5 mol dm(-3) HClO4 saturated with H-2 containing 100 ppm CO was examined on rotating disc ...
Specificity of the UPD of H to the structure of highly dispersed Pt on carbon support
(Pergamon-Elsevier Science Ltd, Oxford, 2007)
Home-made carbon cryogel synthesized by sol-gel polycondensation and freeze-drying is used as support for preparation of highly dispersed Pt catalyst that is made by a modified polyol synthesis method in an ethylene glycol ...
Non-noble metal composite cathodes for hydrogen evolution. Part I: The Ni-MoOx coatings electrodeposited from Watt's type bath containing MoO3 powder particles
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
In this work the Ni-MoOx coatings have been prepared and characterized in view of their possible application as electrocatalysts for hydrogen evolution reaction (HER) in alkaline solution. The procedure of deposition of ...
Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solution. Chemical composition, phase composition and morphology effects
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
In this work the hydrogen evolution reaction (HER) onto Ni-Sn alloy coatings deposited at different current densities from the bath containing 0.1 M Sn2+ and 0.1 M Ni2+ ions in the pyrophosphate-glycine solution, was ...
Non-noble metal composite cathodes for hydrogen evolution. Part II: The Ni-MoO2 coatings electrodeposited from nickel chloride-ammonium chloride bath containing MoO2 powder particles
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
In this work the procedure of the deposition of composite Ni-MoO2 coatings onto Ni mesh from the nickel chloride-ammonium chloride electrolyte containing suspended MoO2 powder particles, under simulated industrial deposition ...
Ni-(Ebonex-supported Ir) composite coatings as electrocatalysts for alkaline water electrolysis. Part I: Hydrogen evolution
(Pergamon-Elsevier Science Ltd, Oxford, 2015)
The hydrogen evolution reaction (HER) was studied at electrodeposited Ni and Ni-(Ebonex/Ir) composite coatings in 1 mol dm(-3) NaOH solution at 25 degrees C. The Ni-(Ebonex/Ir) coatings were electrodeposited from a nickel ...
Service life test of the NiSn coatings as cathodes for hydrogen evolution in industrial chlor-alkali electrolysis
(Pergamon-Elsevier Science Ltd, Oxford, 2014)
In this work the "service life test" (SLT) of the NiSn alloy coatings as cathodes for the hydrogen evolution reaction (HER), deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) ...
Ni-(Ebonex-supported Ir) composite coatings as electrocatalysts for alkaline water electrolysis. Part II: Oxygen evolution
(Pergamon-Elsevier Science Ltd, Oxford, 2016)
The oxygen evolution reaction (OER) was studied at pure Ni and Ni-(Ebonex/Ir) composite coatings in 1 M NaOH solution at 25 degrees C. Ni-(Ebonex-supported Ir) coatings were electro-deposited from a nickel Watts bath ...
Electrodeposited AgPd alloy coatings as efficient catalysts for the ethanol oxidation reaction
(Pergamon-Elsevier Science Ltd, Oxford, 2018)
The Pd and three AgPd alloy layers (AgPd1, AgPd2 and AgPd3) were electrodeposited onto Au disc electrodes from the solution containing high concentration of chloride ions (>12 M). All coatings were investigated by scanning ...
Kinetics of the hydrogen evolution reaction on Ni-(Ebonex-supported Ru) composite coatings in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The hydrogen evolution reaction (HER) was studied on Ni, Ni-Ebonex and Ni-(Ebonex-Ru) coatings in 1 mol dm(-3) NaOH solution at 25 degrees C. The composite coatings were electro-deposited from a nickel Watts-type bath ...