Spectroscopic study of spinel ZnCr2O4 obtained from mechanically activated ZnO-Cr2O3 mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and Cr2O3 powders in equimolar quantities was mechanically activated by grinding using a high energy vibro-mil I for 0, 40 and 80 min. The spinet ZnCr2O4 was prepared from activated mixtures by a ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
Microstructural characterization of mechanically activated ZnO-Cr2O3 system
(Elsevier Sci Ltd, Oxford, 2005)
An equimolar mixtures of starting ZnO and Cr2O3 powders were mechanically activated by grinding using a planetary ball mill for various periods of time (40-320min). Formation of nanocrystalline ZnCr2O4 as normal spine] ...
Preparation of nanostructured Zn-Cr-O spinel powders by ultrasonic spray pyrolysis
(Elsevier Sci Ltd, Oxford, 2001)
Ultrasonic spray pyrolysis (1.7 MHz) has been applied for the generation of zinc chromium oxide submicronic (470 nm) particles from the corresponding metal nitrate solution. Heterogeneous gas-liquid/solid chemical reactions ...