Far infrared properties of sintered NiO
(Elsevier Sci Ltd, Oxford, 2007)
Far infrared reflection spectra of NiO polycrystals sintered at 1100 degrees C for various times (30-240 min) were measured at room temperature using a FTIR Spectrometer-Brucker 113V. The measured spectra depended on the ...
Tailoring of morphology and orientation of LaNiO3 films from polymeric precursors
(Elsevier Sci Ltd, Oxford, 2007)
The aim of this work was to prepare lanthanum nickel oxide (LaNiO3, LNO) thin films of different morphology and orientation. The precursor solutions were prepared by a chemical method from citric salts of lanthanum and ...
Microstructural investigation of the PZT films prepared from the suspension of nanocrystalline powders
(Elsevier Sci Ltd, Oxford, 2004)
PZT thin films of composition Pb(Zr0.52Ti0.48)O-3 were prepared by a novel method from the suspension of nanocrystalline PZT powders. The powders were obtained by mechanochemical synthesis. Films were deposited on silicon ...
Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions
(Elsevier Sci Ltd, Oxford, 2005)
SnO2 varistors doped with CoO, Cr2O3 and Nb2O5 were prepared by evaporation and decomposition of suspensions. The composition of the varistors was optimized to improve electrical properties, such as nonlinearity, leakage ...
Strontium titanate films prepared by spray pyrolysis
(Elsevier Sci Ltd, Oxford, 2004)
Strontium titanate thin films were prepared by spray pyrolysis technique. Deposition parameters, such as solution concentration, time and temperature of deposition, and flow rate of carrier gas were optimized to obtain ...
Screen printed PLZT thick films prepared from nanopowders
(Elsevier Sci Ltd, Oxford, 2007)
The gap between the bulk materials and thin films can be filled with thick films suitably designed and appropriate processed. Thick films of complex system like lead-lanthanum-zirconium titanate (PLZT) is difficult to ...
Spectroscopic study of spinel ZnCr2O4 obtained from mechanically activated ZnO-Cr2O3 mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and Cr2O3 powders in equimolar quantities was mechanically activated by grinding using a high energy vibro-mil I for 0, 40 and 80 min. The spinet ZnCr2O4 was prepared from activated mixtures by a ...
Phase evolution in Ce-doped yttrium-aluminum-based particles derived from aerosol
(Elsevier Sci Ltd, Oxford, 2007)
The common nitrates precursor solution leading to the Y3Al5O12:Ce3+ (YAG:Ce) composition with 2 at.% of cerium, is ultrasonically atomised and introduced into the tubular flow reactor at 320 degrees C. Having in mind that ...
Investigation on possibility of mechanochemical synthesis of CaTiO3 from different precursors
(Elsevier Sci Ltd, Oxford, 2007)
Recently, mechanochemical synthesis was widely used in preparation of perovskite type of materials, such as BaTiO3, PbTiO3, PZT, etc. In this work, the possibility of mechanochemical synthesis of CaTiO3 from different ...
ZnO varistors from intensively milled powders
(Elsevier Sci Ltd, Oxford, 2007)
Two ways of application of intensive milling in ZnO varistors processing were compared. First was intensive milling of mixture of previously prepared constituent phases. In this case, intensive milling was applied only to ...