Investigation on possibility of mechanochemical synthesis of CaTiO3 from different precursors
(Elsevier Sci Ltd, Oxford, 2007)
Recently, mechanochemical synthesis was widely used in preparation of perovskite type of materials, such as BaTiO3, PbTiO3, PZT, etc. In this work, the possibility of mechanochemical synthesis of CaTiO3 from different ...
ZnO varistors with reduced amount of additives prepared by direct mixing of constituent phases
(Elsevier Sci Ltd, Oxford, 2007)
The aim of this work was to reduce number of additives using new method of preparation, refered as "direct mixing of the constituent phases". The method is based on sintering of a mixture of constituent phases with the ...
ZnO varistors from intensively milled powders
(Elsevier Sci Ltd, Oxford, 2007)
Two ways of application of intensive milling in ZnO varistors processing were compared. First was intensive milling of mixture of previously prepared constituent phases. In this case, intensive milling was applied only to ...
Far infrared reflection spectroscopy of Zn2SnO4 ceramics obtained by sintering mechanically activated ZnO-SnO2 powder mixtures
(Elsevier Sci Ltd, Oxford, 2007)
A mixture of starting ZnO and SnO2 powders (molar ratio 2: 1) were mechanically activated for 10, 40, 80 and 160 min in a planetary ball mill and then isothermally sintered at 1300 degrees C for 2 h in order to obtain ...
The nature of structural changes in nanocrystalline ZnO powders under linear heating conditions
(Elsevier Sci Ltd, Oxford, 2004)
The nature of exothermal and irreversible structural changes observed during linear heating of nanocrystalline ZnO powders was investigated using differential scanning calorimetry, X ray, SEM and TEM analysis. Nanocrystalline ...
Microstructural characterization of mechanically activated ZnO-Cr2O3 system
(Elsevier Sci Ltd, Oxford, 2005)
An equimolar mixtures of starting ZnO and Cr2O3 powders were mechanically activated by grinding using a planetary ball mill for various periods of time (40-320min). Formation of nanocrystalline ZnCr2O4 as normal spine] ...