Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Termoelektrična i magnetna svojstva NaCo2-xCuxO4 (x=0; 0,01; 0,03; 0,05) / Thermoelectric and magnetic properties of NaCo2-xCuxO4 (x = 0; 0,01; 0,03; 0,05)
(Univerzitet u Beogradu, Fakultet za fizičku hemiju, 2017)
Predmet ove doktorske disertacije je ispitivanje uticaja dveju različitih metoda sinteze keramičkih prahova i malih količina Cu2+ kao dopanta na fazni i hemijski sastav, mikrostrukturu, termoelektrična i magnetna svojstva ...
Synthesis of BaTiO3 from a mechanically activated BaCO3-TiO2 system
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this article the solid state reaction of BaTiO3 formation from a mechanically activated BaCO3-TiO2 system has been investigated. An equimolar mixture of BaCO3 and TiO2 powders was activated in a planetary ball mill in ...
Ispitivanje sinterovane cink-kalaj-oksidne keramike fotoakustičnom spektroskopijom / Photoacoustic spectroscopy investigation of sintered zinc-tin-oxide ceramics
(Savez hemijskih inženjera, Beograd, 2007)
Prahovi ZnO i SnO2 pomešani u molarnom odnosu 2:1 mehanički su aktivirani u planetarnim mlinu sa kuglama u intervalu od 10 do 160 minuta. Dobijene smeše presovane su i izotermski sinterovane na 1300 °C, dva sata. Uzorci ...
Intrinsic resistivity of sintered nickel manganite vs. powder activation time and density
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2008)
In this work the DC resistivity of sintered nickel manganite NiMn2O4 (NTC thermistor material) was studied as a function of additional powder activation time in a planetary ball mill (0, 5, 15, 30, 45 and 60 min). The ...
Modification of the structural and optical properties of commercial ZnO powder by mechanical activation
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy ...
Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...
Investigation of zinc stannate synthesis using photoacoustic spectroscopy
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2007)
Mixtures of ZnO and SnO2 powders, with molar ratio of 2:1, were mechanically activated for 40, 80 and 160 minutes in a planetary ball mill. The resulting powders were compacted into pellets and non-isothermally sintered ...
Optimization of mechanical activation of fly ash
(Institute for multidisciplinary research, 2019)
More than 5.5 million tonnes of fly ash (FA), a by-product originating from coal combustion in thermal power plants (TPP), is produced in Serbia annually. Only small part of the FA is reused, mostly by cement industry, ...
Structural, electrical and magnetic properties of mechanically activated manganese and zinc ferrite
(Belgrade : Institute for Multidisciplinary Research of the University of Belgrade, 2017)
Starting hematite (Fe2O3), zinc oxide (ZnO) and manganese carbonate (MnCO3) powders were homogenized in a planetary ball mill in stainless steel bowls with stainless steel balls for 15 min, calcined in air at 1000 C for ...