Electrical properties of ZnO varistors prepared by direct mixing of constituent phases
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Varistor samples containing different amounts of constituent phases were prepared by direct mixing of constituent phases. Detailed electrical characterization was performed to explain the influence of minor phases (spinel ...
Electrical properties of mechanically activated zinc oxide
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Microstructural properties of a commercial zinc oxide powder were modified by mechanical activation in a high-energy vibro-mill. The obtained powders were dry pressed and sintered at 1100 degrees C for 2 h. The electrical ...
Sixty years of the theory of B. Ya. Pines
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Modification of the structural and optical properties of commercial ZnO powder by mechanical activation
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Mechanical activation was used as a method for modification of the structural and optical properties of commercial ZnO powder. For this purpose zinc oxide powder was mechanically treated by grinding in a high-energy ...
Analysis of early-stage sintering mechanisms of mechanically activated BaTiO3
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2006)
Barium-titanate powder was mechanically activated in a planetary-ball mill for 60 and 120 minutes. Non-isothermal sintering of non-activated and activated powder samples was investigated using a dilatometer in the temperature ...