Ti substrate coated with composite Cr-MoO2 coatings as highly selective cathode materials in hypochlorite production
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
The aim of this work was to investigate the possibility of preparation of the composite Cr-MoO2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression ...
RuOx nanoparticles deposited on TiO2 nanotube arrays by ion-exchange method as electrocatalysts for the hydrogen evolution reaction in acid solution
(Pergamon-Elsevier Science Ltd, Oxford, 2015)
Nanocomposite cathodes for the hydrogen evolution reaction (HER) were prepared by deposition of RuOx catalyst particles on self-organized titania nanotube (TiNT) arrays of highly developed surface area, following a procedure ...
Ni-Sn coatings as cathodes for hydrogen evolution in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2013)
In this work the hydrogen evolution reaction (HER) at Ni-Sn alloy coatings, deposited onto Ni 40 mesh at different current densities from the bath containing 0.1 mol dm(-3) SnCl2 + 0.3 mol dm(-3) NiCl2 in the pyrophosphate-glycine ...
Voltammetric and differential pulse determination of roxithromycin
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The oxidative behavior of antibiotic roxithromycin standard was studied at a gold electrode in 0.05 M NaHCO3 using cyclic linear sweep voltammetry and differential pulse voltammetry. It was found that the value of the ...
Pt supported on nano-tungsten carbide as a beneficial catalyst for the oxygen reduction reaction in alkaline solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
Platinum nanocatalyst at nano-tungsten carbide was synthesized, characterized and tested for oxygen reduction reaction (ORR) in 0.1 mol dm(-3) NaOH, at 25 degrees C. Tungsten-carbide islands on nano-tungsten particles (WC) ...
Service life test of non-noble metal composite cathodes for hydrogen evolution in sodium hydroxide solution
(Pergamon-Elsevier Science Ltd, Oxford, 2012)
In this work polarization characteristics and "service life" test of the non-noble metal composite coatings Ni-MoOx and Ni-MoO2 for hydrogen evolution reaction (HER) in 32 wt.% NaOH at 90 degrees C were investigated and ...
Phase identification in electrodeposited Ag-Cd alloys by anodic linear sweep voltammetry and X-ray diffraction techniques
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
During electrodeposition of Ag-Cd alloy coatings phenomena of self-organization and formation of spatio-temporal structures can be observed. The difficulties in the determination of the local phase composition in the ...
An attempt to predict the mechanism of Mo-Ni-O powders electrodeposition from the results of their TEM analysis
(Pergamon-Elsevier Science Ltd, Oxford, 2010)
The Mo-Ni-O powders were electrodeposited from ammonium sulfate containing electrolytes with different Mo/Ni ion concentration ratios. The phase composition of these powders was investigated using TEM. EDS and XRD analysis. ...
Nb-TiO2 supported platinum nanocatalyst for oxygen reduction reaction in alkaline solutions
(Pergamon-Elsevier Science Ltd, Oxford, 2011)
Platinum based nanocatalyst at home made Nb-TiO2 support was synthesized and characterized as the catalyst for oxygen reduction reaction in 0.1 mol dm(-3) NaOH, at 25 degrees C. Nb doped TiO2 catalyst support, containing ...
High surface area Pd nanocatalyst on core-shell tungsten based support as a beneficial catalyst for low temperature fuel cells application
(Pergamon-Elsevier Science Ltd, Oxford, 2017)
Tungsten based support was prepared by polycondensation of resorcinol and formaldehyde from ammonium metatungstate, in the presence cetyltrimethylammonium bromide (CTABr) surfactant. Pd nanocatalyst on this support was ...