Nanocrystalline CuAlO2 powder by the nitrate-citrate combustion route
Аутори
Vojisavljević, KatarinaStojanović, Biljana
Khomyakova, Evgeniya
Benčan Golob, Andreja
Kmet, Brigita
Malič, Barbara
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The copper aluminate (CuAlO2) with the delafossite structure has recently drawn attention as a promising p-type semiconducting material. It can be used as a transparent conducting oxide in the field of invisible electronics for production of different optoelectronic devices, but also as a catalyst for conversion of the solar power to hydrogen energy, room temperature ozone sensor, or thermoelectric. The performance of CuAlO2 in some of the mentioned applications could be optimized by increasing the surface area and decreasing its particle size. For that purpose, the nanocrystalline CuAlO2 powder was synthesised by the self-sustained combustion route.
Citric acid was introduced both as the chelating and reducing agent or fuel. The citric acid/metal ion ratio was adjusted to provide fuel-lean, stoichiometric, and fuel-rich conditions of the redox reaction. Equimolar amounts of copper and aluminium nitrates were dissolved in deionized water. Then, the citric acid was added. The solution... was agitated at room temperature for 1 h, and then neutralized to increase the efficiency of the chelating agent. After several hours of drying in the temperature range 60 oC – 80 oC, the sol turned to a homogeneous viscous gel. During the rapid heating, the gel auto-ignited at approximately 250 oC and spontaneously underwent smouldering combustion, forming the grey-black voluminous precursor powder.
According to the X-ray diffraction analysis the phase pure delafossite was obtained only when the precursor powder was prepared from the stoichiometric redox reaction, and after the calcination at 920 oC for 4 h in Ar atmosphere. The field emission scanning electron micrographs revealed the cauliflower aspect of the calcined powder, where small primary particles formed the agglomerates. The formation of the phase pure CuAlO2 powder was also followed by Fourier transformed infrared spectroscopy and confirmed by selective area diffraction analysis.
Кључне речи:
CuAlO2 / combustion synthesis / FE-SEM / Fourier transformed infrared spectroscopy / selective area diffraction analysisИзвор:
Electroceramics XIV Conference 2014, 2014Издавач:
- Edition of Electromeramics Conference
Институција/група
Institut za multidisciplinarna istraživanjaTY - CONF AU - Vojisavljević, Katarina AU - Stojanović, Biljana AU - Khomyakova, Evgeniya AU - Benčan Golob, Andreja AU - Kmet, Brigita AU - Malič, Barbara PY - 2014 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/2920 AB - The copper aluminate (CuAlO2) with the delafossite structure has recently drawn attention as a promising p-type semiconducting material. It can be used as a transparent conducting oxide in the field of invisible electronics for production of different optoelectronic devices, but also as a catalyst for conversion of the solar power to hydrogen energy, room temperature ozone sensor, or thermoelectric. The performance of CuAlO2 in some of the mentioned applications could be optimized by increasing the surface area and decreasing its particle size. For that purpose, the nanocrystalline CuAlO2 powder was synthesised by the self-sustained combustion route. Citric acid was introduced both as the chelating and reducing agent or fuel. The citric acid/metal ion ratio was adjusted to provide fuel-lean, stoichiometric, and fuel-rich conditions of the redox reaction. Equimolar amounts of copper and aluminium nitrates were dissolved in deionized water. Then, the citric acid was added. The solution was agitated at room temperature for 1 h, and then neutralized to increase the efficiency of the chelating agent. After several hours of drying in the temperature range 60 oC – 80 oC, the sol turned to a homogeneous viscous gel. During the rapid heating, the gel auto-ignited at approximately 250 oC and spontaneously underwent smouldering combustion, forming the grey-black voluminous precursor powder. According to the X-ray diffraction analysis the phase pure delafossite was obtained only when the precursor powder was prepared from the stoichiometric redox reaction, and after the calcination at 920 oC for 4 h in Ar atmosphere. The field emission scanning electron micrographs revealed the cauliflower aspect of the calcined powder, where small primary particles formed the agglomerates. The formation of the phase pure CuAlO2 powder was also followed by Fourier transformed infrared spectroscopy and confirmed by selective area diffraction analysis. PB - Edition of Electromeramics Conference C3 - Electroceramics XIV Conference 2014 T1 - Nanocrystalline CuAlO2 powder by the nitrate-citrate combustion route UR - https://hdl.handle.net/21.15107/rcub_rimsi_2920 ER -
@conference{ author = "Vojisavljević, Katarina and Stojanović, Biljana and Khomyakova, Evgeniya and Benčan Golob, Andreja and Kmet, Brigita and Malič, Barbara", year = "2014", abstract = "The copper aluminate (CuAlO2) with the delafossite structure has recently drawn attention as a promising p-type semiconducting material. It can be used as a transparent conducting oxide in the field of invisible electronics for production of different optoelectronic devices, but also as a catalyst for conversion of the solar power to hydrogen energy, room temperature ozone sensor, or thermoelectric. The performance of CuAlO2 in some of the mentioned applications could be optimized by increasing the surface area and decreasing its particle size. For that purpose, the nanocrystalline CuAlO2 powder was synthesised by the self-sustained combustion route. Citric acid was introduced both as the chelating and reducing agent or fuel. The citric acid/metal ion ratio was adjusted to provide fuel-lean, stoichiometric, and fuel-rich conditions of the redox reaction. Equimolar amounts of copper and aluminium nitrates were dissolved in deionized water. Then, the citric acid was added. The solution was agitated at room temperature for 1 h, and then neutralized to increase the efficiency of the chelating agent. After several hours of drying in the temperature range 60 oC – 80 oC, the sol turned to a homogeneous viscous gel. During the rapid heating, the gel auto-ignited at approximately 250 oC and spontaneously underwent smouldering combustion, forming the grey-black voluminous precursor powder. According to the X-ray diffraction analysis the phase pure delafossite was obtained only when the precursor powder was prepared from the stoichiometric redox reaction, and after the calcination at 920 oC for 4 h in Ar atmosphere. The field emission scanning electron micrographs revealed the cauliflower aspect of the calcined powder, where small primary particles formed the agglomerates. The formation of the phase pure CuAlO2 powder was also followed by Fourier transformed infrared spectroscopy and confirmed by selective area diffraction analysis.", publisher = "Edition of Electromeramics Conference", journal = "Electroceramics XIV Conference 2014", title = "Nanocrystalline CuAlO2 powder by the nitrate-citrate combustion route", url = "https://hdl.handle.net/21.15107/rcub_rimsi_2920" }
Vojisavljević, K., Stojanović, B., Khomyakova, E., Benčan Golob, A., Kmet, B.,& Malič, B.. (2014). Nanocrystalline CuAlO2 powder by the nitrate-citrate combustion route. in Electroceramics XIV Conference 2014 Edition of Electromeramics Conference.. https://hdl.handle.net/21.15107/rcub_rimsi_2920
Vojisavljević K, Stojanović B, Khomyakova E, Benčan Golob A, Kmet B, Malič B. Nanocrystalline CuAlO2 powder by the nitrate-citrate combustion route. in Electroceramics XIV Conference 2014. 2014;. https://hdl.handle.net/21.15107/rcub_rimsi_2920 .
Vojisavljević, Katarina, Stojanović, Biljana, Khomyakova, Evgeniya, Benčan Golob, Andreja, Kmet, Brigita, Malič, Barbara, "Nanocrystalline CuAlO2 powder by the nitrate-citrate combustion route" in Electroceramics XIV Conference 2014 (2014), https://hdl.handle.net/21.15107/rcub_rimsi_2920 .