Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures

Menićanin, Aleksandar; Živanov, Ljiljana D; Stojanović, Goran M; Samardžić, Nataša M; Randjelović, Danijela V

doi:10.1109/TED.2013.2274661

Samo za registrovane korisnike

2013

Autori

Menićanin, Aleksandar

Živanov, Ljiljana D

Stojanović, Goran M

Samardžić, Nataša M
Randjelović, Danijela V

Članak u časopisu (Objavljena verzija)

Metapodaci

Prikaz svih podataka o dokumentu

Apstrakt

This brief presents the transport parameters of silver layers on a polyimide substrate fabricated by an inkjet printing technology using nanoparticle inks with 20 wt% and 40 wt% silver. All the electrical characteristics of the samples were measured by Hall effect measurement system at 0.37 T. The electron mobility in inkjet printed silver layer was 7.07 and 4.58 cm(2)/V s for 20 wt% silver, 29.6 and 21.3 cm(2)/V s for 40 wt% silver at 77 and 300 K, respectively. The resistivity in inkjet printed silver layer with 20 wt% is 20.6 x 10(-6) and 27.1 x 10(-6) Omega cm, and 4.81 x 10(-6) and 8.27 x 10(-6) Omega cm for 40 wt% silver at 77 and 300 K, respectively. The surface morphology and profiles of the samples were obtained with an atomic force and scanning electron microscope.

Ključne reči:

silver nanoparticle ink / inkjet printing / Hall measurement / Flexible technology

Izvor:
IEEE Transactions on Electron Devices, 2013, 60, 9, 2963-2967

Izdavač:

IEEE-Inst Electrical Electronics Engineers Inc, Piscataway

Finansiranje / projekti:

Project APOSTILLE [256615]
Inovativne elektronske komponente i sistemi bazirani na neorganskim i organskim tehnologijama ugrađeni u robe i proizvode široke potrošnje (RS-32016)
0-3D nanostrukture za primenu u elektronici i obnovljivim izvorima energije: sinteza, karakterizacija i procesiranje (RS-45007)
Mikro, nano-sistemi i senzori za primenu u elektroprivredi, procesnoj industriji i zaštiti životne sredine (RS-32008)

DOI: 10.1109/TED.2013.2274661

ISSN: 0018-9383

WoS: 000323640300040

Scopus: 2-s2.0-84883286875

[ Google Scholar ]


	8
	8

TY  - JOUR
AU  - Menićanin, Aleksandar
AU  - Živanov, Ljiljana D
AU  - Stojanović, Goran M
AU  - Samardžić, Nataša M
AU  - Randjelović, Danijela V
PY  - 2013
UR  - http://rimsi.imsi.bg.ac.rs/handle/123456789/718
AB  - This brief presents the transport parameters of silver layers on a polyimide substrate fabricated by an inkjet printing technology using nanoparticle inks with 20 wt% and 40 wt% silver. All the electrical characteristics of the samples were measured by Hall effect measurement system at 0.37 T. The electron mobility in inkjet printed silver layer was 7.07 and 4.58 cm(2)/V s for 20 wt% silver, 29.6 and 21.3 cm(2)/V s for 40 wt% silver at 77 and 300 K, respectively. The resistivity in inkjet printed silver layer with 20 wt% is 20.6 x 10(-6) and 27.1 x 10(-6) Omega cm, and 4.81 x 10(-6) and 8.27 x 10(-6) Omega cm for 40 wt% silver at 77 and 300 K, respectively. The surface morphology and profiles of the samples were obtained with an atomic force and scanning electron microscope.
PB  - IEEE-Inst Electrical Electronics Engineers Inc, Piscataway
T2  - IEEE Transactions on Electron Devices
T1  - Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures
EP  - 2967
IS  - 9
SP  - 2963
VL  - 60
DO  - 10.1109/TED.2013.2274661
ER  -

@article{
author = "Menićanin, Aleksandar and Živanov, Ljiljana D and Stojanović, Goran M and Samardžić, Nataša M and Randjelović, Danijela V",
year = "2013",
abstract = "This brief presents the transport parameters of silver layers on a polyimide substrate fabricated by an inkjet printing technology using nanoparticle inks with 20 wt% and 40 wt% silver. All the electrical characteristics of the samples were measured by Hall effect measurement system at 0.37 T. The electron mobility in inkjet printed silver layer was 7.07 and 4.58 cm(2)/V s for 20 wt% silver, 29.6 and 21.3 cm(2)/V s for 40 wt% silver at 77 and 300 K, respectively. The resistivity in inkjet printed silver layer with 20 wt% is 20.6 x 10(-6) and 27.1 x 10(-6) Omega cm, and 4.81 x 10(-6) and 8.27 x 10(-6) Omega cm for 40 wt% silver at 77 and 300 K, respectively. The surface morphology and profiles of the samples were obtained with an atomic force and scanning electron microscope.",
publisher = "IEEE-Inst Electrical Electronics Engineers Inc, Piscataway",
journal = "IEEE Transactions on Electron Devices",
title = "Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures",
pages = "2967-2963",
number = "9",
volume = "60",
doi = "10.1109/TED.2013.2274661"
}

Menićanin, A., Živanov, L. D., Stojanović, G. M., Samardžić, N. M.,& Randjelović, D. V.. (2013). Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures. in IEEE Transactions on Electron Devices
IEEE-Inst Electrical Electronics Engineers Inc, Piscataway., 60(9), 2963-2967.
https://doi.org/10.1109/TED.2013.2274661

Menićanin A, Živanov LD, Stojanović GM, Samardžić NM, Randjelović DV. Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures. in IEEE Transactions on Electron Devices. 2013;60(9):2963-2967.
doi:10.1109/TED.2013.2274661 .

Menićanin, Aleksandar, Živanov, Ljiljana D, Stojanović, Goran M, Samardžić, Nataša M, Randjelović, Danijela V, "Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures" in IEEE Transactions on Electron Devices, 60, no. 9 (2013):2963-2967,
https://doi.org/10.1109/TED.2013.2274661 . .