Mechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates
Апстракт
In this paper, the main activity was to investigate how different substrates, temperature of sintering and percentage of silver ink containing silver nanoparticles influence on Young's modulus and hardness of printed silver thin samples. Samples were prepared by low cost ink-jet printing technique using Dimatix Material Printer on polyimide flexible substrate and slide glass. Characterization of these samples was carried out by Nano Indenter using a three sided pyramidal (Berkovich) diamond tip. Measurement results show that the thickness of ink-jet printed silver layer varies for different percent of nanoparticles in silver ink. All measurements were done at same depth of indentation to avoid possibility of perforation of printed layer. The higher temperature of sintering and the higher percent of silver nanoparticles give the bigger Young's modulus and hardness of printed silver sample. This research provides very useful information about mechanical characterization of the silver lay...ers on flexible substrates for printed-electronics.
Кључне речи:
silver nanoparticle ink / nanoindentation / ink-jet printingИзвор:
IFIP Advances in Information and Communication Technology, 2013, 394, 133-141Издавач:
- Springer New York LLC
Финансирање / пројекти:
- Иновативне електронске компоненте и системи базирани на неорганским и органским технологијама уграђени у робе и производе широке потрошње (RS-32016)
- EC FP7 project APOSTILLE [256615]
DOI: 10.1007/978-3-642-37291-9_15
ISSN: 1868-4238
WoS: 000323186100015
Scopus: 2-s2.0-84913603400
Институција/група
Institut za multidisciplinarna istraživanjaTY - JOUR AU - Vasiljević, D.Z. AU - Menicanin, Aleksandar AU - Živanov, Ljiljana D PY - 2013 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/624 AB - In this paper, the main activity was to investigate how different substrates, temperature of sintering and percentage of silver ink containing silver nanoparticles influence on Young's modulus and hardness of printed silver thin samples. Samples were prepared by low cost ink-jet printing technique using Dimatix Material Printer on polyimide flexible substrate and slide glass. Characterization of these samples was carried out by Nano Indenter using a three sided pyramidal (Berkovich) diamond tip. Measurement results show that the thickness of ink-jet printed silver layer varies for different percent of nanoparticles in silver ink. All measurements were done at same depth of indentation to avoid possibility of perforation of printed layer. The higher temperature of sintering and the higher percent of silver nanoparticles give the bigger Young's modulus and hardness of printed silver sample. This research provides very useful information about mechanical characterization of the silver layers on flexible substrates for printed-electronics. PB - Springer New York LLC T2 - IFIP Advances in Information and Communication Technology T1 - Mechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates EP - 141 SP - 133 VL - 394 DO - 10.1007/978-3-642-37291-9_15 ER -
@article{ author = "Vasiljević, D.Z. and Menicanin, Aleksandar and Živanov, Ljiljana D", year = "2013", abstract = "In this paper, the main activity was to investigate how different substrates, temperature of sintering and percentage of silver ink containing silver nanoparticles influence on Young's modulus and hardness of printed silver thin samples. Samples were prepared by low cost ink-jet printing technique using Dimatix Material Printer on polyimide flexible substrate and slide glass. Characterization of these samples was carried out by Nano Indenter using a three sided pyramidal (Berkovich) diamond tip. Measurement results show that the thickness of ink-jet printed silver layer varies for different percent of nanoparticles in silver ink. All measurements were done at same depth of indentation to avoid possibility of perforation of printed layer. The higher temperature of sintering and the higher percent of silver nanoparticles give the bigger Young's modulus and hardness of printed silver sample. This research provides very useful information about mechanical characterization of the silver layers on flexible substrates for printed-electronics.", publisher = "Springer New York LLC", journal = "IFIP Advances in Information and Communication Technology", title = "Mechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates", pages = "141-133", volume = "394", doi = "10.1007/978-3-642-37291-9_15" }
Vasiljević, D.Z., Menicanin, A.,& Živanov, L. D.. (2013). Mechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates. in IFIP Advances in Information and Communication Technology Springer New York LLC., 394, 133-141. https://doi.org/10.1007/978-3-642-37291-9_15
Vasiljević D, Menicanin A, Živanov LD. Mechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates. in IFIP Advances in Information and Communication Technology. 2013;394:133-141. doi:10.1007/978-3-642-37291-9_15 .
Vasiljević, D.Z., Menicanin, Aleksandar, Živanov, Ljiljana D, "Mechanical Characterization of Ink-Jet Printed Ag Samples on Different Substrates" in IFIP Advances in Information and Communication Technology, 394 (2013):133-141, https://doi.org/10.1007/978-3-642-37291-9_15 . .