Magnetic properties of pure and Ca and Sr doped LaMnO3 prepared by polymerisable complex method
Apstrakt
In this work, pure and Ca2+ and Sr2+ doped LaMnO3 powders were obtained using polymerisable complex method from citrate precursors. La2O3, Mn(NO3)(2) and citric acid were used for citrate formation, and ethylene glycol was later added as polymerisation agent. For the preparation of doped samples, solutions of Ca(CH3COO)(2) and Sr(NO3)(2) were used. Calcination was performed at 800 degrees C for 6 h in oxygen atmosphere. X-ray diffraction analysis showed that single phase LaMnO3, La0.7Ca0.3MnO3, La0.7Sr0.3MnO3 and La0.7Ca0.15Sr0.15MnO3 powders were obtained. Morphology of prepared samples was analysed using SEM analysis. Field cooled and zero field cooled magnetisations versus temperature and hysteresis loops of powders and sintered samples were analysed. Curie temperatures were in the range from 170 to 370 K, depending on composition. Measured magnetisations even reached 85 emu g(-1). The influence of dopants on magnetisation, Curie temperature and hysteresis loops were quantified and ...discussed.
Ključne reči:
Polymerisation complex method / Magnetic properties / Magnerisation / Lanthanum manganiteIzvor:
Advances in Applied Ceramics, 2009, 108, 5, 267-272Izdavač:
- Maney Publishing, Leeds
DOI: 10.1179/174367609X414026
ISSN: 1743-6753
WoS: 000268173900003
Scopus: 2-s2.0-70449489525
Institucija/grupa
Institut za multidisciplinarna istraživanjaTY - JOUR AU - Branković, Goran AU - Duris, K. AU - Jaglicic, Z. AU - Jagodic, M. AU - Branković, Zorica PY - 2009 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/338 AB - In this work, pure and Ca2+ and Sr2+ doped LaMnO3 powders were obtained using polymerisable complex method from citrate precursors. La2O3, Mn(NO3)(2) and citric acid were used for citrate formation, and ethylene glycol was later added as polymerisation agent. For the preparation of doped samples, solutions of Ca(CH3COO)(2) and Sr(NO3)(2) were used. Calcination was performed at 800 degrees C for 6 h in oxygen atmosphere. X-ray diffraction analysis showed that single phase LaMnO3, La0.7Ca0.3MnO3, La0.7Sr0.3MnO3 and La0.7Ca0.15Sr0.15MnO3 powders were obtained. Morphology of prepared samples was analysed using SEM analysis. Field cooled and zero field cooled magnetisations versus temperature and hysteresis loops of powders and sintered samples were analysed. Curie temperatures were in the range from 170 to 370 K, depending on composition. Measured magnetisations even reached 85 emu g(-1). The influence of dopants on magnetisation, Curie temperature and hysteresis loops were quantified and discussed. PB - Maney Publishing, Leeds T2 - Advances in Applied Ceramics T1 - Magnetic properties of pure and Ca and Sr doped LaMnO3 prepared by polymerisable complex method EP - 272 IS - 5 SP - 267 VL - 108 DO - 10.1179/174367609X414026 ER -
@article{ author = "Branković, Goran and Duris, K. and Jaglicic, Z. and Jagodic, M. and Branković, Zorica", year = "2009", abstract = "In this work, pure and Ca2+ and Sr2+ doped LaMnO3 powders were obtained using polymerisable complex method from citrate precursors. La2O3, Mn(NO3)(2) and citric acid were used for citrate formation, and ethylene glycol was later added as polymerisation agent. For the preparation of doped samples, solutions of Ca(CH3COO)(2) and Sr(NO3)(2) were used. Calcination was performed at 800 degrees C for 6 h in oxygen atmosphere. X-ray diffraction analysis showed that single phase LaMnO3, La0.7Ca0.3MnO3, La0.7Sr0.3MnO3 and La0.7Ca0.15Sr0.15MnO3 powders were obtained. Morphology of prepared samples was analysed using SEM analysis. Field cooled and zero field cooled magnetisations versus temperature and hysteresis loops of powders and sintered samples were analysed. Curie temperatures were in the range from 170 to 370 K, depending on composition. Measured magnetisations even reached 85 emu g(-1). The influence of dopants on magnetisation, Curie temperature and hysteresis loops were quantified and discussed.", publisher = "Maney Publishing, Leeds", journal = "Advances in Applied Ceramics", title = "Magnetic properties of pure and Ca and Sr doped LaMnO3 prepared by polymerisable complex method", pages = "272-267", number = "5", volume = "108", doi = "10.1179/174367609X414026" }
Branković, G., Duris, K., Jaglicic, Z., Jagodic, M.,& Branković, Z.. (2009). Magnetic properties of pure and Ca and Sr doped LaMnO3 prepared by polymerisable complex method. in Advances in Applied Ceramics Maney Publishing, Leeds., 108(5), 267-272. https://doi.org/10.1179/174367609X414026
Branković G, Duris K, Jaglicic Z, Jagodic M, Branković Z. Magnetic properties of pure and Ca and Sr doped LaMnO3 prepared by polymerisable complex method. in Advances in Applied Ceramics. 2009;108(5):267-272. doi:10.1179/174367609X414026 .
Branković, Goran, Duris, K., Jaglicic, Z., Jagodic, M., Branković, Zorica, "Magnetic properties of pure and Ca and Sr doped LaMnO3 prepared by polymerisable complex method" in Advances in Applied Ceramics, 108, no. 5 (2009):267-272, https://doi.org/10.1179/174367609X414026 . .