Analysis of isothermal sintering of zinc-titanate doped with MgO
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, Ti02 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes in a planetary ball mill. The powders obtained were pressed under different pressures and the results were fitted with a phenomenological compacting equation. Isothermal sintering was performed in air for 120 minutes at four different temperatures. Structural characterization of ZnO-TiOrMgb system' after milling and sintering was performed at room temperature using XRPD measurements. DTA measurements showed different activation energies for pure and doped ZnO-Ti02 systems. The main conclusions are that doped zinc titanate samples achieve higher densities after sintering and that addition of MgO stabilizes the crystal structure of zinc titanate.
Кључне речи:
barium titanate / isothermal sintering / ball millingИзвор:
VII Scientific Meeting Physics and Technology of Materials - FITEM '07, 2007, 27-27Издавач:
- Čačak : Technical Faculty
Напомена:
- Conference poster: https://hdl.handle.net/21.15107/rcub_dais_313
- The final results were published in the paper: http://dx.doi.org/10.2298/SOS0703241O
Повезане информације:
Институција/група
Institut za multidisciplinarna istraživanjaTY - CONF AU - Obradović, Nina AU - Stevanović, Suzana AU - Mitrić, Miodrag AU - Nikolić, Maria Vesna AU - Ristić, Momčilo M. PY - 2007 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/1642 AB - The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, Ti02 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes in a planetary ball mill. The powders obtained were pressed under different pressures and the results were fitted with a phenomenological compacting equation. Isothermal sintering was performed in air for 120 minutes at four different temperatures. Structural characterization of ZnO-TiOrMgb system' after milling and sintering was performed at room temperature using XRPD measurements. DTA measurements showed different activation energies for pure and doped ZnO-Ti02 systems. The main conclusions are that doped zinc titanate samples achieve higher densities after sintering and that addition of MgO stabilizes the crystal structure of zinc titanate. PB - Čačak : Technical Faculty C3 - VII Scientific Meeting Physics and Technology of Materials - FITEM '07 T1 - Analysis of isothermal sintering of zinc-titanate doped with MgO EP - 27 SP - 27 UR - https://hdl.handle.net/21.15107/rcub_dais_632 ER -
@conference{ author = "Obradović, Nina and Stevanović, Suzana and Mitrić, Miodrag and Nikolić, Maria Vesna and Ristić, Momčilo M.", year = "2007", abstract = "The aim of this work was analysis of isothermal sintering of zinc titanate ceramics doped with MgO obtained by mechanical activation. Mixtures of ZnO, Ti02 and MgO (0, 1.25 and 2.5%) were mechanically activated 15 minutes in a planetary ball mill. The powders obtained were pressed under different pressures and the results were fitted with a phenomenological compacting equation. Isothermal sintering was performed in air for 120 minutes at four different temperatures. Structural characterization of ZnO-TiOrMgb system' after milling and sintering was performed at room temperature using XRPD measurements. DTA measurements showed different activation energies for pure and doped ZnO-Ti02 systems. The main conclusions are that doped zinc titanate samples achieve higher densities after sintering and that addition of MgO stabilizes the crystal structure of zinc titanate.", publisher = "Čačak : Technical Faculty", journal = "VII Scientific Meeting Physics and Technology of Materials - FITEM '07", title = "Analysis of isothermal sintering of zinc-titanate doped with MgO", pages = "27-27", url = "https://hdl.handle.net/21.15107/rcub_dais_632" }
Obradović, N., Stevanović, S., Mitrić, M., Nikolić, M. V.,& Ristić, M. M.. (2007). Analysis of isothermal sintering of zinc-titanate doped with MgO. in VII Scientific Meeting Physics and Technology of Materials - FITEM '07 Čačak : Technical Faculty., 27-27. https://hdl.handle.net/21.15107/rcub_dais_632
Obradović N, Stevanović S, Mitrić M, Nikolić MV, Ristić MM. Analysis of isothermal sintering of zinc-titanate doped with MgO. in VII Scientific Meeting Physics and Technology of Materials - FITEM '07. 2007;:27-27. https://hdl.handle.net/21.15107/rcub_dais_632 .
Obradović, Nina, Stevanović, Suzana, Mitrić, Miodrag, Nikolić, Maria Vesna, Ristić, Momčilo M., "Analysis of isothermal sintering of zinc-titanate doped with MgO" in VII Scientific Meeting Physics and Technology of Materials - FITEM '07 (2007):27-27, https://hdl.handle.net/21.15107/rcub_dais_632 .