Densification rate and phase structure changes during sintering of zinc titanate ceramics
(Elsevier Sci Ltd, Oxford, 2009)
Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Sintering was performed in a dilatometer in two regimes: the first to 900 degrees C (heating rates 5, 10 and 15 degrees ...
Dielectric and ferroelectric properties of BST ceramics obtained by a hydrothermally assisted complex polymerization method
(Elsevier Sci Ltd, Oxford, 2015)
Ba0.8Sr0.2TiO3 (BST) powder, obtained by a hydrothermal treatment of precursor solution previously prepared by a complex polymerization method (HT-CPM), was uniaxially pressed and sintered at 1280 degrees C for 1-32 h. The ...
Effect of preparation route on the microstructure and electrical conductivity of co-doped ceria
(Elsevier Sci Ltd, Oxford, 2013)
Dense Ce0.8Sm0.1Gd0.1O2-delta electrolytes were fabricated by sintering of CeO2 solid solutions which were prepared from metal nitrates and NaOH using self propagating room temperature synthesis (SPRT). Three different ...
Antimony doping effect on barium titanate structure and electrical properties
(Elsevier Sci Ltd, Oxford, 2011)
Nanopowders of pure and antimony doped barium titanate (BaTiO3-BT) were synthesized by polymeric precursors method based on Pechini process. Obtained powders were pressed and sintered at 1300 degrees C for 8 h. XRD analysis ...
Structural and electrical properties of sintered Fe2O3/TiO2 nanopowder mixtures
(Elsevier Sci Ltd, Oxford, 2014)
Starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) were mixed in the weight ratios 60:40 and 40:60. Green samples were sintered in the temperature range 750-1250 degrees C in air. Structural, morphological ...
Nanostructured Fe2O3/TiO2 thick films: Analysis of structural and electronic properties
(Elsevier Sci Ltd, Oxford, 2015)
Thick films using starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) mixed in the weight ratios 60:40 and 40:60 for thick film paste were fabricated by screen printing technology on an alumina substrate. ...