Synthesis, characterization and electrocatalytical behavior of Nb-TiO2/Pt nanocatalyst for oxygen reduction reaction
(Elsevier Science Bv, Amsterdam, 2010)
In order to point out the effect of the support to the catalyst for oxygen reduction reaction nano-crystalline Nb-doped TiO2 was synthesized through a modified sol-gel route procedure. The specific surface area of the ...
Structure study of nanosized La- and Sb-doped BaTiO3
(Elsevier Science Sa, Lausanne, 2010)
Lanthanum and antimony doped barium titanate powders were prepared by polymeric precursors method through Pechini process. Obtained powder was pressed into pellet and sintering was performed at 1300 degrees C for 8 h. The ...
Preparation of ultrathin PZT films by a chemical solution deposition method from a polymeric citrate precursor
(Elsevier Sci Ltd, Oxford, 2010)
Ultrathin PZT film was prepared using a chemical solution deposition method from polymeric citrate precursors. The PZT solution was spin-coated on an amorphous silica layer formed on a Si(l 0 0) substrate. The films were ...
The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis
(Elsevier Sci Ltd, Oxford, 2010)
BaTiO3 ceramic powders were prepared by a complex method based on the Pechini type reaction route and mechanically assisted synthesis. In both ways BaTiO3 ceramics were sintered after 120 min on 1300 degrees C without ...
Dielectric and relaxor behavior of BaBi4Ti4O15 ceramics
(Elsevier Science Sa, Lausanne, 2010)
Barium bismuth titanate BaBi4Ti4O15 (BBiT) ceramics have been prepared using non-conventional solid-state reaction route based on mechanochemical synthesis during intensive milling. The X-ray diffraction method was used ...
Multiferroic bismuth manganite prepared by mechanochemical synthesis
(Elsevier Sci Ltd, Oxford, 2010)
Multiferroic bismuth manganite (BiMnO3) is known as a material that exhibits both ferromagnetic and ferroelectric properties making it interesting for various technological applications. Unfortunately, preparation of BiMnO3 ...
Mechanical and microstructural properties of alkali-activated fly ash geopolymers
(Elsevier, Amsterdam, 2010)
This paper investigates the properties of geopolymer obtained by alkali-activation of fly ash (FA), i.e. the influence of characteristics of the representative group of FA (class F) from Serbia, as well as that of the ...