FAR INFRARED AND MICROSTRUCTURAL STUDIES OF MECHANICALLY ACTIVATED NICKEL MANGANITE
(Institute for Multidisciplinary Research, University of Belgrade, 2011)
Nickel manganite powder was mechanically activated in a high energy planetary ball
mill for 5-60 min. Then the powders were pressed and sintered for 60 minutes at 9000C,
10500C and 12000C. Morphological changes of nickel ...
VARIATION IN OPTICAL AND ELECTRONIC PROPERTIES OF ZnO INDUCED BY MECHANICAL MILLING AND THERMAL TREATMENT
(Institute for Multidisciplinary Research, University of Belgrade, 2011)
Zinc oxide ceramics have been prepared from ZnO powders obtained by mechanical
milling for 300 min in air in different high-energy mills. Structural disorder induced in
ZnO powder by mechanical activation (MA) and partial ...