PZT ceramics obtained from mechanochemically synthesized powders
Само за регистроване кориснике
2003
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.
Кључне речи:
Piezo ceramics / PZT / Piezoelectric properties / MechanochemistryИзвор:
Journal of Materials Science-Materials in Electronics, 2003, 14, 1, 37-41Издавач:
- Kluwer Academic Publ, Dordrecht
DOI: 10.1023/A:1021527615661
ISSN: 0957-4522
WoS: 000179704600008
Scopus: 2-s2.0-0037287151
Институција/група
Institut za multidisciplinarna istraživanjaTY - JOUR AU - Branković, Zorica AU - Branković, Goran AU - Varela, JA PY - 2003 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/82 AB - PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability. PB - Kluwer Academic Publ, Dordrecht T2 - Journal of Materials Science-Materials in Electronics T1 - PZT ceramics obtained from mechanochemically synthesized powders EP - 41 IS - 1 SP - 37 VL - 14 DO - 10.1023/A:1021527615661 ER -
@article{ author = "Branković, Zorica and Branković, Goran and Varela, JA", year = "2003", abstract = "PZT ceramics were obtained from the mechanochemically synthesized powders. Milling and sintering conditions were optimized based on results of density measurements, as well as on microstructural and electrical characterization. As a result, highly dense and homogeneous ceramics were obtained. Excellent microstructural properties resulted in good electrical properties. Samples showed values of dielectric constants reaching 12800 at the Curie temperature, as well as low dielectric loss under the optimal processing conditions. High values of remanent polarization, reaching 60 muC cm(-2), indicate high internal polarizability.", publisher = "Kluwer Academic Publ, Dordrecht", journal = "Journal of Materials Science-Materials in Electronics", title = "PZT ceramics obtained from mechanochemically synthesized powders", pages = "41-37", number = "1", volume = "14", doi = "10.1023/A:1021527615661" }
Branković, Z., Branković, G.,& Varela, J.. (2003). PZT ceramics obtained from mechanochemically synthesized powders. in Journal of Materials Science-Materials in Electronics Kluwer Academic Publ, Dordrecht., 14(1), 37-41. https://doi.org/10.1023/A:1021527615661
Branković Z, Branković G, Varela J. PZT ceramics obtained from mechanochemically synthesized powders. in Journal of Materials Science-Materials in Electronics. 2003;14(1):37-41. doi:10.1023/A:1021527615661 .
Branković, Zorica, Branković, Goran, Varela, JA, "PZT ceramics obtained from mechanochemically synthesized powders" in Journal of Materials Science-Materials in Electronics, 14, no. 1 (2003):37-41, https://doi.org/10.1023/A:1021527615661 . .