Thermoelectric Cu doped sodium cobaltite – structural, magnetic and mechanical properties
Authors
Perać, Sanja![](/themes/MirageRIMSI/images/orcid.png)
Savic, Slavica
Branković, Zorica
![](/themes/MirageRIMSI/images/orcid.png)
Bernik, Slavko
Radojković, Aleksandar
![](/themes/MirageRIMSI/images/orcid.png)
Branković, Goran
![](/themes/MirageRIMSI/images/orcid.png)
Conference object (Published version)
![](/themes/MirageRIMSI//images/creativecommons/arr.png)
Metadata
Show full item recordAbstract
With the increase of the consumption of electrical energy, the need for new energy sources is growing. Conversion of waste heat into electricity, based on the thermoelectric effects is one of the ways to produce the electrical energy. Layered cobalt oxides have been the subject of many investigations in past decade as candidates for application in energy conversion. The ceramic sodium cobaltite became a promising candidate for potential thermoelectric applications, because of its large thermopower and low resistivity. In this work, polycrystalline samples of NaCo2–xCuxO4 (x = 0, 0.01, 0.03, 0.05) were synthesized from the powder precursors obtained by the citric acid complex method (CAC) and mechanochemically assisted solid state reaction method (MASSR). The obtained powders were uniaxially pressed into disc-shaped pellets and subsequently sintered at 880 °C in inert argon atmosphere. Thermoelectric parameters (the electrical resistivity (ρ), the thermal conductivity (κ) and the Seebec...k coefficient (S)) were measured in two temperature regions. In the first one (between 2 and 300 K) κ and S were measured by a Quantum Design physical property measurement system (PPMS 9T) equipped with a 9 T magnet and ρ by a standard four-terminal technique using the direct current. In the second, all parameters were measured simultaneously, in the temperature gradient (ΔT) between hot and cold sides of the samples using Z- meter, based on the “large ΔT method”, and the figure of merit (ZT) was subsequen tly calculated. Accordingly, ρ, κ and S were determined for a temperature gradient that is established between the hot and cold sides of the samples at the time of each measurement; thus the obtained values represented the actual thermoelectric response of a material under conditions of application. In the low temperature range the highest figure of merit of 0.022 at 300 K was observed for the CAC sample doped with 1 mol% Cu, and it was almost twice higher than in the undoped sample confirming the significant influence of Cu-doping with even small concentrations. As for the results obtained in the temperature gradient, the highest ZT value of 0.061 at T = 473 K was observed for the sample with 5 mol% of Cu prepared by the CAC method. Sample magnetization was measured using a Quantum Design SQUID MPMS-XL-5 magnetometer in zero field cooled (ZFC) and field cooled (FC) regimes, between 2 K and 300 K and in the applied field of 100 Oe. The magnetic susceptibility (χ) of all samples followed the Curie-Weiss law in the temperature range between 50 K and 300 K, while a negative Weiss constant (θ) implied an antiferromagnetic interaction. Indentation experiments were carried out to investigate mechanical properties, therefore, the hardness (H) and the Young's modulus of elasticity (Y) were determined using Agilent Nanoindenter G200. It was found that the highest Y (65.2 GPa) and H (1.41 GPa) were obtained for the CAC sample containing 1 mol% of Cu. These results indicated a significant improvement of mechanical properties even in the case of the sample with the lowest dopant concentration. In general, better thermoelectric and mechanic properties showed the samples synthesized by the CAC method, confirming that fine, homogeneous precursor powders present a good base for obtaining material with improved thermoelectric performances.
Keywords:
Thermoelectric properties / Mechanical properties / Figure og merit / Magnetic susceptibility / Sodium cobaltiteSource:
7th Conference of the Serbian Society for Ceramic Materials, 2023, 59-Publisher:
- Institut za multidisciplinarna istraživanja Kneza Višeslava 1, 11000 Belgrade, Serbia
Funding / projects:
Collections
Institution/Community
Institut za multidisciplinarna istraživanjaTY - CONF AU - Perać, Sanja AU - Savic, Slavica AU - Branković, Zorica AU - Bernik, Slavko AU - Radojković, Aleksandar AU - Branković, Goran PY - 2023 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/2213 AB - With the increase of the consumption of electrical energy, the need for new energy sources is growing. Conversion of waste heat into electricity, based on the thermoelectric effects is one of the ways to produce the electrical energy. Layered cobalt oxides have been the subject of many investigations in past decade as candidates for application in energy conversion. The ceramic sodium cobaltite became a promising candidate for potential thermoelectric applications, because of its large thermopower and low resistivity. In this work, polycrystalline samples of NaCo2–xCuxO4 (x = 0, 0.01, 0.03, 0.05) were synthesized from the powder precursors obtained by the citric acid complex method (CAC) and mechanochemically assisted solid state reaction method (MASSR). The obtained powders were uniaxially pressed into disc-shaped pellets and subsequently sintered at 880 °C in inert argon atmosphere. Thermoelectric parameters (the electrical resistivity (ρ), the thermal conductivity (κ) and the Seebeck coefficient (S)) were measured in two temperature regions. In the first one (between 2 and 300 K) κ and S were measured by a Quantum Design physical property measurement system (PPMS 9T) equipped with a 9 T magnet and ρ by a standard four-terminal technique using the direct current. In the second, all parameters were measured simultaneously, in the temperature gradient (ΔT) between hot and cold sides of the samples using Z- meter, based on the “large ΔT method”, and the figure of merit (ZT) was subsequen tly calculated. Accordingly, ρ, κ and S were determined for a temperature gradient that is established between the hot and cold sides of the samples at the time of each measurement; thus the obtained values represented the actual thermoelectric response of a material under conditions of application. In the low temperature range the highest figure of merit of 0.022 at 300 K was observed for the CAC sample doped with 1 mol% Cu, and it was almost twice higher than in the undoped sample confirming the significant influence of Cu-doping with even small concentrations. As for the results obtained in the temperature gradient, the highest ZT value of 0.061 at T = 473 K was observed for the sample with 5 mol% of Cu prepared by the CAC method. Sample magnetization was measured using a Quantum Design SQUID MPMS-XL-5 magnetometer in zero field cooled (ZFC) and field cooled (FC) regimes, between 2 K and 300 K and in the applied field of 100 Oe. The magnetic susceptibility (χ) of all samples followed the Curie-Weiss law in the temperature range between 50 K and 300 K, while a negative Weiss constant (θ) implied an antiferromagnetic interaction. Indentation experiments were carried out to investigate mechanical properties, therefore, the hardness (H) and the Young's modulus of elasticity (Y) were determined using Agilent Nanoindenter G200. It was found that the highest Y (65.2 GPa) and H (1.41 GPa) were obtained for the CAC sample containing 1 mol% of Cu. These results indicated a significant improvement of mechanical properties even in the case of the sample with the lowest dopant concentration. In general, better thermoelectric and mechanic properties showed the samples synthesized by the CAC method, confirming that fine, homogeneous precursor powders present a good base for obtaining material with improved thermoelectric performances. PB - Institut za multidisciplinarna istraživanja Kneza Višeslava 1, 11000 Belgrade, Serbia C3 - 7th Conference of the Serbian Society for Ceramic Materials T1 - Thermoelectric Cu doped sodium cobaltite – structural, magnetic and mechanical properties SP - 59 UR - https://hdl.handle.net/21.15107/rcub_rimsi_2213 ER -
@conference{ author = "Perać, Sanja and Savic, Slavica and Branković, Zorica and Bernik, Slavko and Radojković, Aleksandar and Branković, Goran", year = "2023", abstract = "With the increase of the consumption of electrical energy, the need for new energy sources is growing. Conversion of waste heat into electricity, based on the thermoelectric effects is one of the ways to produce the electrical energy. Layered cobalt oxides have been the subject of many investigations in past decade as candidates for application in energy conversion. The ceramic sodium cobaltite became a promising candidate for potential thermoelectric applications, because of its large thermopower and low resistivity. In this work, polycrystalline samples of NaCo2–xCuxO4 (x = 0, 0.01, 0.03, 0.05) were synthesized from the powder precursors obtained by the citric acid complex method (CAC) and mechanochemically assisted solid state reaction method (MASSR). The obtained powders were uniaxially pressed into disc-shaped pellets and subsequently sintered at 880 °C in inert argon atmosphere. Thermoelectric parameters (the electrical resistivity (ρ), the thermal conductivity (κ) and the Seebeck coefficient (S)) were measured in two temperature regions. In the first one (between 2 and 300 K) κ and S were measured by a Quantum Design physical property measurement system (PPMS 9T) equipped with a 9 T magnet and ρ by a standard four-terminal technique using the direct current. In the second, all parameters were measured simultaneously, in the temperature gradient (ΔT) between hot and cold sides of the samples using Z- meter, based on the “large ΔT method”, and the figure of merit (ZT) was subsequen tly calculated. Accordingly, ρ, κ and S were determined for a temperature gradient that is established between the hot and cold sides of the samples at the time of each measurement; thus the obtained values represented the actual thermoelectric response of a material under conditions of application. In the low temperature range the highest figure of merit of 0.022 at 300 K was observed for the CAC sample doped with 1 mol% Cu, and it was almost twice higher than in the undoped sample confirming the significant influence of Cu-doping with even small concentrations. As for the results obtained in the temperature gradient, the highest ZT value of 0.061 at T = 473 K was observed for the sample with 5 mol% of Cu prepared by the CAC method. Sample magnetization was measured using a Quantum Design SQUID MPMS-XL-5 magnetometer in zero field cooled (ZFC) and field cooled (FC) regimes, between 2 K and 300 K and in the applied field of 100 Oe. The magnetic susceptibility (χ) of all samples followed the Curie-Weiss law in the temperature range between 50 K and 300 K, while a negative Weiss constant (θ) implied an antiferromagnetic interaction. Indentation experiments were carried out to investigate mechanical properties, therefore, the hardness (H) and the Young's modulus of elasticity (Y) were determined using Agilent Nanoindenter G200. It was found that the highest Y (65.2 GPa) and H (1.41 GPa) were obtained for the CAC sample containing 1 mol% of Cu. These results indicated a significant improvement of mechanical properties even in the case of the sample with the lowest dopant concentration. In general, better thermoelectric and mechanic properties showed the samples synthesized by the CAC method, confirming that fine, homogeneous precursor powders present a good base for obtaining material with improved thermoelectric performances.", publisher = "Institut za multidisciplinarna istraživanja Kneza Višeslava 1, 11000 Belgrade, Serbia", journal = "7th Conference of the Serbian Society for Ceramic Materials", title = "Thermoelectric Cu doped sodium cobaltite – structural, magnetic and mechanical properties", pages = "59", url = "https://hdl.handle.net/21.15107/rcub_rimsi_2213" }
Perać, S., Savic, S., Branković, Z., Bernik, S., Radojković, A.,& Branković, G.. (2023). Thermoelectric Cu doped sodium cobaltite – structural, magnetic and mechanical properties. in 7th Conference of the Serbian Society for Ceramic Materials Institut za multidisciplinarna istraživanja Kneza Višeslava 1, 11000 Belgrade, Serbia., 59. https://hdl.handle.net/21.15107/rcub_rimsi_2213
Perać S, Savic S, Branković Z, Bernik S, Radojković A, Branković G. Thermoelectric Cu doped sodium cobaltite – structural, magnetic and mechanical properties. in 7th Conference of the Serbian Society for Ceramic Materials. 2023;:59. https://hdl.handle.net/21.15107/rcub_rimsi_2213 .
Perać, Sanja, Savic, Slavica, Branković, Zorica, Bernik, Slavko, Radojković, Aleksandar, Branković, Goran, "Thermoelectric Cu doped sodium cobaltite – structural, magnetic and mechanical properties" in 7th Conference of the Serbian Society for Ceramic Materials (2023):59, https://hdl.handle.net/21.15107/rcub_rimsi_2213 .