Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions
Само за регистроване кориснике
2005
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
SnO2 varistors doped with CoO, Cr2O3 and Nb2O5 were prepared by evaporation and decomposition of suspensions. The composition of the varistors was optimized to improve electrical properties, such as nonlinearity, leakage current and electrical stability. The best results were achieved with the following composition: 99.15% SnO2 +0.75% CoO+0.05% Cr2O3 +0.05% Nb2O5. Samples showed high density, reaching 99.5% of the theoretical density, as well as an homogeneous microstructure. The nonlinear coefficient was higher than 30 in the current range from 10(-7) to 10(-2) A/cm(2). The leakage current was 0.86 mu A/cm(2). These samples showed high stability of electrical parameters when they were exposed to high current of 27 mA/cm(2) for different time periods up to 30 min.
Кључне речи:
varistor / electrical propertiesИзвор:
Journal of the European Ceramic Society, 2005, 25, 12, 3011-3015Издавач:
- Elsevier Sci Ltd, Oxford
DOI: 10.1016/j.jeurceramsoc.2005.04.001
ISSN: 0955-2219
WoS: 000230569300213
Scopus: 2-s2.0-20444483256
Институција/група
Institut za multidisciplinarna istraživanjaTY - JOUR AU - Branković, Goran AU - Branković, Zorica AU - Varela, JA PY - 2005 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/116 AB - SnO2 varistors doped with CoO, Cr2O3 and Nb2O5 were prepared by evaporation and decomposition of suspensions. The composition of the varistors was optimized to improve electrical properties, such as nonlinearity, leakage current and electrical stability. The best results were achieved with the following composition: 99.15% SnO2 +0.75% CoO+0.05% Cr2O3 +0.05% Nb2O5. Samples showed high density, reaching 99.5% of the theoretical density, as well as an homogeneous microstructure. The nonlinear coefficient was higher than 30 in the current range from 10(-7) to 10(-2) A/cm(2). The leakage current was 0.86 mu A/cm(2). These samples showed high stability of electrical parameters when they were exposed to high current of 27 mA/cm(2) for different time periods up to 30 min. PB - Elsevier Sci Ltd, Oxford T2 - Journal of the European Ceramic Society T1 - Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions EP - 3015 IS - 12 SP - 3011 VL - 25 DO - 10.1016/j.jeurceramsoc.2005.04.001 ER -
@article{ author = "Branković, Goran and Branković, Zorica and Varela, JA", year = "2005", abstract = "SnO2 varistors doped with CoO, Cr2O3 and Nb2O5 were prepared by evaporation and decomposition of suspensions. The composition of the varistors was optimized to improve electrical properties, such as nonlinearity, leakage current and electrical stability. The best results were achieved with the following composition: 99.15% SnO2 +0.75% CoO+0.05% Cr2O3 +0.05% Nb2O5. Samples showed high density, reaching 99.5% of the theoretical density, as well as an homogeneous microstructure. The nonlinear coefficient was higher than 30 in the current range from 10(-7) to 10(-2) A/cm(2). The leakage current was 0.86 mu A/cm(2). These samples showed high stability of electrical parameters when they were exposed to high current of 27 mA/cm(2) for different time periods up to 30 min.", publisher = "Elsevier Sci Ltd, Oxford", journal = "Journal of the European Ceramic Society", title = "Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions", pages = "3015-3011", number = "12", volume = "25", doi = "10.1016/j.jeurceramsoc.2005.04.001" }
Branković, G., Branković, Z.,& Varela, J.. (2005). Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions. in Journal of the European Ceramic Society Elsevier Sci Ltd, Oxford., 25(12), 3011-3015. https://doi.org/10.1016/j.jeurceramsoc.2005.04.001
Branković G, Branković Z, Varela J. Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions. in Journal of the European Ceramic Society. 2005;25(12):3011-3015. doi:10.1016/j.jeurceramsoc.2005.04.001 .
Branković, Goran, Branković, Zorica, Varela, JA, "Nonlinear properties and stability of SnO2 varistors prepared by evaporation and decomposition of suspensions" in Journal of the European Ceramic Society, 25, no. 12 (2005):3011-3015, https://doi.org/10.1016/j.jeurceramsoc.2005.04.001 . .