Photocatalytic degradation of textile dye with hydrothermally modified nanoanatase
Аутори
Simović, BojanaPoleti, Dejan
Kovač, Sabina
Bjelajac, Andjelika
Dapčević, Aleksandra
Brankovic, Goran
Конференцијски прилог (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
The environmental friendly materials based on titanium oxides are often chosen
for the industrial application due to their extraordinary characteristics (biological
and chemical stability, good photocatalitic activity, wide band gap and costeffectiveness). On the other hand, the hydrothermal process in alkaline solutions
became a very important treatment in the production of titania and titanate
nanostructures. The aim of this work was to investigate how different conditions of
hydrothermal treatment could modify the structural, microstructural and
photocatalytic properties of starting nanoanatase.
Nanoanatase powder was hydrothermally treated with NaOH solution (c =
5 mol/dm) at different temperatures (T = 110, 135 and 160 °C) and durations (t = 6,
12 and 18 h). The obtained samples were washed out with distilled water,
centrifuged and dried. Nine specimens are prepared and labeled as AT–t
, where T is
temperature of the treatment and t is duration of the treatment. The na...nocrystalline
samples were characterized by XRD, TEM/SAED and FESEM techniques. The
photocatalytic activity was tested on the Reactive Orange 16 (RO16) textile azo dye.
The XRD analysis showed that the hydrothermal treatment caused the formation
of a secondary phase (H2Ti2O5·H2O, PDF 47–0124) besides anatase. This is due to
the reaction between anatase and NaOH. The increase of temperature and/or time
increases the amount of secondary phase. For example, the specimen A110–6 contains
about 12 wt.% of H2Ti2O5·H2O, while the content of this phase amounts about
37 wt.% in A135–12. The average crystallite size of all samples was smaller than 20
nm. This was comfirmed by TEM. The FESEM revealed soft agglomerates created
from nanoparticles.
The photocatalytic experiments showed that the presence of secondary phase
decreases the photocatalytic activity. For example, A110–6 decolorized 35 % of the
RO16 dye within 90 minutes, while A135–12 degraded only 15% of the same dye in
the same time interval.
Кључне речи:
Hydrothermally modified nanoanatase / Titanate / Photocatalysis / Reactive orange 16Извор:
3rd Conference of the Serbian Society for Ceramic Materials, Belgrade, Serbia, Programme and the Book of Abstracts, 2015, 82-Издавач:
- Institut za multidisciplinarna istraživanja, Belgrade, Serbia
Финансирање / пројекти:
- 0-3D наноструктуре за примену у електроници и обновљивим изворима енергије: синтеза, карактеризација и процесирање (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45007)
Институција/група
Institut za multidisciplinarna istraživanjaTY - CONF AU - Simović, Bojana AU - Poleti, Dejan AU - Kovač, Sabina AU - Bjelajac, Andjelika AU - Dapčević, Aleksandra AU - Brankovic, Goran PY - 2015 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/3093 AB - The environmental friendly materials based on titanium oxides are often chosen for the industrial application due to their extraordinary characteristics (biological and chemical stability, good photocatalitic activity, wide band gap and costeffectiveness). On the other hand, the hydrothermal process in alkaline solutions became a very important treatment in the production of titania and titanate nanostructures. The aim of this work was to investigate how different conditions of hydrothermal treatment could modify the structural, microstructural and photocatalytic properties of starting nanoanatase. Nanoanatase powder was hydrothermally treated with NaOH solution (c = 5 mol/dm) at different temperatures (T = 110, 135 and 160 °C) and durations (t = 6, 12 and 18 h). The obtained samples were washed out with distilled water, centrifuged and dried. Nine specimens are prepared and labeled as AT–t , where T is temperature of the treatment and t is duration of the treatment. The nanocrystalline samples were characterized by XRD, TEM/SAED and FESEM techniques. The photocatalytic activity was tested on the Reactive Orange 16 (RO16) textile azo dye. The XRD analysis showed that the hydrothermal treatment caused the formation of a secondary phase (H2Ti2O5·H2O, PDF 47–0124) besides anatase. This is due to the reaction between anatase and NaOH. The increase of temperature and/or time increases the amount of secondary phase. For example, the specimen A110–6 contains about 12 wt.% of H2Ti2O5·H2O, while the content of this phase amounts about 37 wt.% in A135–12. The average crystallite size of all samples was smaller than 20 nm. This was comfirmed by TEM. The FESEM revealed soft agglomerates created from nanoparticles. The photocatalytic experiments showed that the presence of secondary phase decreases the photocatalytic activity. For example, A110–6 decolorized 35 % of the RO16 dye within 90 minutes, while A135–12 degraded only 15% of the same dye in the same time interval. PB - Institut za multidisciplinarna istraživanja, Belgrade, Serbia C3 - 3rd Conference of the Serbian Society for Ceramic Materials, Belgrade, Serbia, Programme and the Book of Abstracts T1 - Photocatalytic degradation of textile dye with hydrothermally modified nanoanatase SP - 82 UR - https://hdl.handle.net/21.15107/rcub_rimsi_3093 ER -
@conference{ author = "Simović, Bojana and Poleti, Dejan and Kovač, Sabina and Bjelajac, Andjelika and Dapčević, Aleksandra and Brankovic, Goran", year = "2015", abstract = "The environmental friendly materials based on titanium oxides are often chosen for the industrial application due to their extraordinary characteristics (biological and chemical stability, good photocatalitic activity, wide band gap and costeffectiveness). On the other hand, the hydrothermal process in alkaline solutions became a very important treatment in the production of titania and titanate nanostructures. The aim of this work was to investigate how different conditions of hydrothermal treatment could modify the structural, microstructural and photocatalytic properties of starting nanoanatase. Nanoanatase powder was hydrothermally treated with NaOH solution (c = 5 mol/dm) at different temperatures (T = 110, 135 and 160 °C) and durations (t = 6, 12 and 18 h). The obtained samples were washed out with distilled water, centrifuged and dried. Nine specimens are prepared and labeled as AT–t , where T is temperature of the treatment and t is duration of the treatment. The nanocrystalline samples were characterized by XRD, TEM/SAED and FESEM techniques. The photocatalytic activity was tested on the Reactive Orange 16 (RO16) textile azo dye. The XRD analysis showed that the hydrothermal treatment caused the formation of a secondary phase (H2Ti2O5·H2O, PDF 47–0124) besides anatase. This is due to the reaction between anatase and NaOH. The increase of temperature and/or time increases the amount of secondary phase. For example, the specimen A110–6 contains about 12 wt.% of H2Ti2O5·H2O, while the content of this phase amounts about 37 wt.% in A135–12. The average crystallite size of all samples was smaller than 20 nm. This was comfirmed by TEM. The FESEM revealed soft agglomerates created from nanoparticles. The photocatalytic experiments showed that the presence of secondary phase decreases the photocatalytic activity. For example, A110–6 decolorized 35 % of the RO16 dye within 90 minutes, while A135–12 degraded only 15% of the same dye in the same time interval.", publisher = "Institut za multidisciplinarna istraživanja, Belgrade, Serbia", journal = "3rd Conference of the Serbian Society for Ceramic Materials, Belgrade, Serbia, Programme and the Book of Abstracts", title = "Photocatalytic degradation of textile dye with hydrothermally modified nanoanatase", pages = "82", url = "https://hdl.handle.net/21.15107/rcub_rimsi_3093" }
Simović, B., Poleti, D., Kovač, S., Bjelajac, A., Dapčević, A.,& Brankovic, G.. (2015). Photocatalytic degradation of textile dye with hydrothermally modified nanoanatase. in 3rd Conference of the Serbian Society for Ceramic Materials, Belgrade, Serbia, Programme and the Book of Abstracts Institut za multidisciplinarna istraživanja, Belgrade, Serbia., 82. https://hdl.handle.net/21.15107/rcub_rimsi_3093
Simović B, Poleti D, Kovač S, Bjelajac A, Dapčević A, Brankovic G. Photocatalytic degradation of textile dye with hydrothermally modified nanoanatase. in 3rd Conference of the Serbian Society for Ceramic Materials, Belgrade, Serbia, Programme and the Book of Abstracts. 2015;:82. https://hdl.handle.net/21.15107/rcub_rimsi_3093 .
Simović, Bojana, Poleti, Dejan, Kovač, Sabina, Bjelajac, Andjelika, Dapčević, Aleksandra, Brankovic, Goran, "Photocatalytic degradation of textile dye with hydrothermally modified nanoanatase" in 3rd Conference of the Serbian Society for Ceramic Materials, Belgrade, Serbia, Programme and the Book of Abstracts (2015):82, https://hdl.handle.net/21.15107/rcub_rimsi_3093 .