HIGHLY CONDUCTIVE LANTHANOIDE STABILIZED δ-Bi2O3 PHASES
Апстракт
Due to the increasing demands for new highly efficient and environmentally
friendly energy conversion technologies, the oxide ion conductors applicable in
solid oxide fuel cells (SOFCs) have widely been investigated. The aim is to find a
suitable electrolyte with the ionic conductivity high enough at intermediate
temperatures in order to reduce the operating temperature of SOFCs. The high
temperature δ-Bi2O3 phase has been proposed as a good candidate for electrolyte in
SOFCs because it is the fastest known ionic conductor.
In this study, the possibility to stabilize O
2–
ion conductors related to the -Bi2O3
polymorph in Bi2O3–Tm2O3 and Bi2O3–Lu2O3 systems was investigated. Six starting
mixtures with the following compositions (Bi1–xTmx)2O3, x = 0.11, 0.14 and 0.20,
and (Bi1–yLuy)2O3, y = 0.15, 0.20 and 0.25, were dry homogenized in an agate
mortar, heat treated at 750 °C for 3 h and then slowly furnace cooled. The samples
were characterized by XRD, TEM/SAED, SEM, DTA an...d SEI techniques.
Based on XRD and TEM/SAED, the targeted cubic δ-Bi2O3 single-phase
samples (space group
Fm3m
) were successfully obtained within all six systems. The
unit cell parameter of both Tm- and Lu-doped -Bi2O3 decreases as dopant content
increases. By comparing Tm- and Lu-doped δ-Bi2O3 phases mutually, an expected
increase of the unit cell parameters with larger ionic radii of dopant was found
[ri(Tm3+) = 0.88 Å, and ri(Lu3+) = 0.86 Å in the octahedral environment1
].
Electrochemical impedance of -Bi2O3 phases was measured between 300 and
800 °C. At temperatures 550 – 800 °C the conductivities are of the same order of
magnitude (0.1 – 0.4 S cm
–1
), but with lowering temperature they rapidly decrease
resulting in two activation energies. This is due to the changes in conductivity
mechanism which will be discussed.According to the cyclic DTA curves, no phase
transitions were observed in the following samples: (Bi0.8Tm0.2)2O3, (Bi0.8Lu0.2)2O3
and (Bi0.75Lu0.25)2O3, indicating that these -Bi2O3 phases are stable within the
whole investigated interval, i.e., from room temperature to 985 °C. This means that
the application of these electrolyte materials could result not only in the significant
enhancement of IT-SOFC electrochemical performance, but also in their good
structural stability over long time service in a wide temperature range.
1. R. D. Shannon, Acta Cryst. A, 32 (1976) 751
Кључне речи:
d-Bi2O3 / lanthanoides / ionic conductivityИзвор:
3rd Conference of the Serbian Society for Ceramic Materials, 2015, 63-Издавач:
- Društvo za keramičke materijale Srbije
Финансирање / пројекти:
- 0-3D наноструктуре за примену у електроници и обновљивим изворима енергије: синтеза, карактеризација и процесирање (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45007)
Институција/група
Institut za multidisciplinarna istraživanjaTY - CONF AU - Dapčevć, Aleksandra AU - Dejan, Poleti AU - Rogan, Jelena AU - Radojković, Aleksandar AU - Branković, Goran PY - 2015 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/2831 AB - Due to the increasing demands for new highly efficient and environmentally friendly energy conversion technologies, the oxide ion conductors applicable in solid oxide fuel cells (SOFCs) have widely been investigated. The aim is to find a suitable electrolyte with the ionic conductivity high enough at intermediate temperatures in order to reduce the operating temperature of SOFCs. The high temperature δ-Bi2O3 phase has been proposed as a good candidate for electrolyte in SOFCs because it is the fastest known ionic conductor. In this study, the possibility to stabilize O 2– ion conductors related to the -Bi2O3 polymorph in Bi2O3–Tm2O3 and Bi2O3–Lu2O3 systems was investigated. Six starting mixtures with the following compositions (Bi1–xTmx)2O3, x = 0.11, 0.14 and 0.20, and (Bi1–yLuy)2O3, y = 0.15, 0.20 and 0.25, were dry homogenized in an agate mortar, heat treated at 750 °C for 3 h and then slowly furnace cooled. The samples were characterized by XRD, TEM/SAED, SEM, DTA and SEI techniques. Based on XRD and TEM/SAED, the targeted cubic δ-Bi2O3 single-phase samples (space group Fm3m ) were successfully obtained within all six systems. The unit cell parameter of both Tm- and Lu-doped -Bi2O3 decreases as dopant content increases. By comparing Tm- and Lu-doped δ-Bi2O3 phases mutually, an expected increase of the unit cell parameters with larger ionic radii of dopant was found [ri(Tm3+) = 0.88 Å, and ri(Lu3+) = 0.86 Å in the octahedral environment1 ]. Electrochemical impedance of -Bi2O3 phases was measured between 300 and 800 °C. At temperatures 550 – 800 °C the conductivities are of the same order of magnitude (0.1 – 0.4 S cm –1 ), but with lowering temperature they rapidly decrease resulting in two activation energies. This is due to the changes in conductivity mechanism which will be discussed.According to the cyclic DTA curves, no phase transitions were observed in the following samples: (Bi0.8Tm0.2)2O3, (Bi0.8Lu0.2)2O3 and (Bi0.75Lu0.25)2O3, indicating that these -Bi2O3 phases are stable within the whole investigated interval, i.e., from room temperature to 985 °C. This means that the application of these electrolyte materials could result not only in the significant enhancement of IT-SOFC electrochemical performance, but also in their good structural stability over long time service in a wide temperature range. 1. R. D. Shannon, Acta Cryst. A, 32 (1976) 751 PB - Društvo za keramičke materijale Srbije C3 - 3rd Conference of the Serbian Society for Ceramic Materials T1 - HIGHLY CONDUCTIVE LANTHANOIDE STABILIZED δ-Bi2O3 PHASES SP - 63 UR - https://hdl.handle.net/21.15107/rcub_rimsi_2831 ER -
@conference{ author = "Dapčevć, Aleksandra and Dejan, Poleti and Rogan, Jelena and Radojković, Aleksandar and Branković, Goran", year = "2015", abstract = "Due to the increasing demands for new highly efficient and environmentally friendly energy conversion technologies, the oxide ion conductors applicable in solid oxide fuel cells (SOFCs) have widely been investigated. The aim is to find a suitable electrolyte with the ionic conductivity high enough at intermediate temperatures in order to reduce the operating temperature of SOFCs. The high temperature δ-Bi2O3 phase has been proposed as a good candidate for electrolyte in SOFCs because it is the fastest known ionic conductor. In this study, the possibility to stabilize O 2– ion conductors related to the -Bi2O3 polymorph in Bi2O3–Tm2O3 and Bi2O3–Lu2O3 systems was investigated. Six starting mixtures with the following compositions (Bi1–xTmx)2O3, x = 0.11, 0.14 and 0.20, and (Bi1–yLuy)2O3, y = 0.15, 0.20 and 0.25, were dry homogenized in an agate mortar, heat treated at 750 °C for 3 h and then slowly furnace cooled. The samples were characterized by XRD, TEM/SAED, SEM, DTA and SEI techniques. Based on XRD and TEM/SAED, the targeted cubic δ-Bi2O3 single-phase samples (space group Fm3m ) were successfully obtained within all six systems. The unit cell parameter of both Tm- and Lu-doped -Bi2O3 decreases as dopant content increases. By comparing Tm- and Lu-doped δ-Bi2O3 phases mutually, an expected increase of the unit cell parameters with larger ionic radii of dopant was found [ri(Tm3+) = 0.88 Å, and ri(Lu3+) = 0.86 Å in the octahedral environment1 ]. Electrochemical impedance of -Bi2O3 phases was measured between 300 and 800 °C. At temperatures 550 – 800 °C the conductivities are of the same order of magnitude (0.1 – 0.4 S cm –1 ), but with lowering temperature they rapidly decrease resulting in two activation energies. This is due to the changes in conductivity mechanism which will be discussed.According to the cyclic DTA curves, no phase transitions were observed in the following samples: (Bi0.8Tm0.2)2O3, (Bi0.8Lu0.2)2O3 and (Bi0.75Lu0.25)2O3, indicating that these -Bi2O3 phases are stable within the whole investigated interval, i.e., from room temperature to 985 °C. This means that the application of these electrolyte materials could result not only in the significant enhancement of IT-SOFC electrochemical performance, but also in their good structural stability over long time service in a wide temperature range. 1. R. D. Shannon, Acta Cryst. A, 32 (1976) 751", publisher = "Društvo za keramičke materijale Srbije", journal = "3rd Conference of the Serbian Society for Ceramic Materials", title = "HIGHLY CONDUCTIVE LANTHANOIDE STABILIZED δ-Bi2O3 PHASES", pages = "63", url = "https://hdl.handle.net/21.15107/rcub_rimsi_2831" }
Dapčevć, A., Dejan, P., Rogan, J., Radojković, A.,& Branković, G.. (2015). HIGHLY CONDUCTIVE LANTHANOIDE STABILIZED δ-Bi2O3 PHASES. in 3rd Conference of the Serbian Society for Ceramic Materials Društvo za keramičke materijale Srbije., 63. https://hdl.handle.net/21.15107/rcub_rimsi_2831
Dapčevć A, Dejan P, Rogan J, Radojković A, Branković G. HIGHLY CONDUCTIVE LANTHANOIDE STABILIZED δ-Bi2O3 PHASES. in 3rd Conference of the Serbian Society for Ceramic Materials. 2015;:63. https://hdl.handle.net/21.15107/rcub_rimsi_2831 .
Dapčevć, Aleksandra, Dejan, Poleti, Rogan, Jelena, Radojković, Aleksandar, Branković, Goran, "HIGHLY CONDUCTIVE LANTHANOIDE STABILIZED δ-Bi2O3 PHASES" in 3rd Conference of the Serbian Society for Ceramic Materials (2015):63, https://hdl.handle.net/21.15107/rcub_rimsi_2831 .