Electrical and sensing properties of indium-doped barium cerate
Аутори
Malešević, AleksandarRadojković, Aleksandar
Žunić, Milan
Savic, Slavica
Perać, Sanja
Branković, Zorica
Branković, Goran
Чланак у часопису (Рецензирана верзија)
Метаподаци
Приказ свих података о документуАпстракт
Systematic analysis of electrical characteristics of BaCe0.75In0.25O3-δ (BCI25) sintered sample was performed in a
dry and a wet argon atmosphere in the 250 ◦C–700 ◦C temperature range. The water vapor sensing properties of
BCI25 porous film and its response and recovery times were investigated under different conditions of temperature
and water vapor concentration. The 30 μm thick film obtained from the powder calcined at 1050 ◦C
exhibited sensitivity comparable to that of the sintered sample with a significantly shorter response and recovery
times. While the sensitivity of the film gradually decreased with a decrease in partial pressure of water vapor (p
(H2O)), a noticeable sensitivity was still observed at p(H2O) of 200 Pa. Decrease in conductivity depended
logarithmically on the partial pressure of water with the slope of 0.52 that is close to the theoretical value. After
several cycles, the reusability test proved an almost unchanged ratio between the impedance value in t...he dry and
the wet Ar atmosphere (p(H2O) = 2.34 kPa), which implied that BCI25, having good stability and sensitivity, is a
promising high-temperature humidity sensor.
Кључне речи:
Ionic conductivity, Perovskites, Sensors, BaCeO3Извор:
Ceramics International, 2023, 49, 15673-15679Издавач:
- Elsevier Ltd
- Techna Group S.r.l.
Финансирање / пројекти:
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200053 (Универзитет у Београду, Институт за мултидисциплинарна истраживања) (RS-MESTD-inst-2020-200053)
- Министарство науке, технолошког развоја и иновација Републике Србије, институционално финансирање - 200358 (BioSense институт) (RS-MESTD-inst-2020-200358)
Институција/група
Institut za multidisciplinarna istraživanjaTY - JOUR AU - Malešević, Aleksandar AU - Radojković, Aleksandar AU - Žunić, Milan AU - Savic, Slavica AU - Perać, Sanja AU - Branković, Zorica AU - Branković, Goran PY - 2023 UR - http://rimsi.imsi.bg.ac.rs/handle/123456789/2299 AB - Systematic analysis of electrical characteristics of BaCe0.75In0.25O3-δ (BCI25) sintered sample was performed in a dry and a wet argon atmosphere in the 250 ◦C–700 ◦C temperature range. The water vapor sensing properties of BCI25 porous film and its response and recovery times were investigated under different conditions of temperature and water vapor concentration. The 30 μm thick film obtained from the powder calcined at 1050 ◦C exhibited sensitivity comparable to that of the sintered sample with a significantly shorter response and recovery times. While the sensitivity of the film gradually decreased with a decrease in partial pressure of water vapor (p (H2O)), a noticeable sensitivity was still observed at p(H2O) of 200 Pa. Decrease in conductivity depended logarithmically on the partial pressure of water with the slope of 0.52 that is close to the theoretical value. After several cycles, the reusability test proved an almost unchanged ratio between the impedance value in the dry and the wet Ar atmosphere (p(H2O) = 2.34 kPa), which implied that BCI25, having good stability and sensitivity, is a promising high-temperature humidity sensor. PB - Elsevier Ltd PB - Techna Group S.r.l. T2 - Ceramics International T1 - Electrical and sensing properties of indium-doped barium cerate EP - 15679 SP - 15673 VL - 49 DO - 10.1016/j.ceramint.2023.01.159 ER -
@article{ author = "Malešević, Aleksandar and Radojković, Aleksandar and Žunić, Milan and Savic, Slavica and Perać, Sanja and Branković, Zorica and Branković, Goran", year = "2023", abstract = "Systematic analysis of electrical characteristics of BaCe0.75In0.25O3-δ (BCI25) sintered sample was performed in a dry and a wet argon atmosphere in the 250 ◦C–700 ◦C temperature range. The water vapor sensing properties of BCI25 porous film and its response and recovery times were investigated under different conditions of temperature and water vapor concentration. The 30 μm thick film obtained from the powder calcined at 1050 ◦C exhibited sensitivity comparable to that of the sintered sample with a significantly shorter response and recovery times. While the sensitivity of the film gradually decreased with a decrease in partial pressure of water vapor (p (H2O)), a noticeable sensitivity was still observed at p(H2O) of 200 Pa. Decrease in conductivity depended logarithmically on the partial pressure of water with the slope of 0.52 that is close to the theoretical value. After several cycles, the reusability test proved an almost unchanged ratio between the impedance value in the dry and the wet Ar atmosphere (p(H2O) = 2.34 kPa), which implied that BCI25, having good stability and sensitivity, is a promising high-temperature humidity sensor.", publisher = "Elsevier Ltd, Techna Group S.r.l.", journal = "Ceramics International", title = "Electrical and sensing properties of indium-doped barium cerate", pages = "15679-15673", volume = "49", doi = "10.1016/j.ceramint.2023.01.159" }
Malešević, A., Radojković, A., Žunić, M., Savic, S., Perać, S., Branković, Z.,& Branković, G.. (2023). Electrical and sensing properties of indium-doped barium cerate. in Ceramics International Elsevier Ltd., 49, 15673-15679. https://doi.org/10.1016/j.ceramint.2023.01.159
Malešević A, Radojković A, Žunić M, Savic S, Perać S, Branković Z, Branković G. Electrical and sensing properties of indium-doped barium cerate. in Ceramics International. 2023;49:15673-15679. doi:10.1016/j.ceramint.2023.01.159 .
Malešević, Aleksandar, Radojković, Aleksandar, Žunić, Milan, Savic, Slavica, Perać, Sanja, Branković, Zorica, Branković, Goran, "Electrical and sensing properties of indium-doped barium cerate" in Ceramics International, 49 (2023):15673-15679, https://doi.org/10.1016/j.ceramint.2023.01.159 . .