Characterisation of Mn0.63Zn0.37Fe2O4 Powders After Intensive Milling and Subsequent Thermal Treatment
(Međunarodni Institut za nauku o sinterovanju, Beograd, 2017)
Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. %) was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes ...
Densification rate and phase structure changes during sintering of zinc titanate ceramics
(Elsevier Sci Ltd, Oxford, 2009)
Densification rate and phase structure changes during sintering of nanosized ZnTiO3 were studied. Sintering was performed in a dilatometer in two regimes: the first to 900 degrees C (heating rates 5, 10 and 15 degrees ...
Nanostructured Fe2O3/TiO2 thick films: Analysis of structural and electronic properties
(Elsevier Sci Ltd, Oxford, 2015)
Thick films using starting nanopowders of TiO2 (anatase 99.7%) and alpha-Fe2O3 (hematite) mixed in the weight ratios 60:40 and 40:60 for thick film paste were fabricated by screen printing technology on an alumina substrate. ...
Influence of mechanochemical activation on the sintering of cordierite ceramics in the presence of Bi2O3 as a functional additive
(Elsevier, Amsterdam, 2012)
Due to its outstanding electrical characteristics, such as the low temperature expansion coefficient, low dielectric constant and good mechanical properties, cordierite, 2MgO center dot 2Al(2)O(3)center dot 5SiO(2), is a ...
Change in structural, ferroelectric, and magnetic properties of bismuth ferrite induced by doping with gadolinium
(Elsevier Sci Ltd, Oxford, 2019)
Bismuth ferrite, BiFeO3, was doped with a wide range of concentrations (0-30%) of Gd in order to investigate structural, ferroelectric, and magnetic properties and their correlation. Powder samples of Bi1-xGdxFeO3 (x = ...
Study on bi-layered ceramics powders prepared by the mechanochemical synthesis
(Elsevier Science Sa, Lausanne, 2009)
Bi-layered structured ferroelectric materials-bismuth titanate, Bi4Ti3O12 (BIT) and barium-bismuth titanate, BaBi4Ti4O15 (BBT) powders were prepared by homogenization and sintering of mixture of stehiometric quantities of ...
The characterization of the barium titanate ceramic powders prepared by the Pechini type reaction route and mechanically assisted synthesis
(Elsevier Sci Ltd, Oxford, 2010)
BaTiO3 ceramic powders were prepared by a complex method based on the Pechini type reaction route and mechanically assisted synthesis. In both ways BaTiO3 ceramics were sintered after 120 min on 1300 degrees C without ...
Antimony doping effect on barium titanate structure and electrical properties
(Elsevier Sci Ltd, Oxford, 2011)
Nanopowders of pure and antimony doped barium titanate (BaTiO3-BT) were synthesized by polymeric precursors method based on Pechini process. Obtained powders were pressed and sintered at 1300 degrees C for 8 h. XRD analysis ...
Dielectric and ferroelectric properties of BST ceramics obtained by a hydrothermally assisted complex polymerization method
(Elsevier Sci Ltd, Oxford, 2015)
Ba0.8Sr0.2TiO3 (BST) powder, obtained by a hydrothermal treatment of precursor solution previously prepared by a complex polymerization method (HT-CPM), was uniaxially pressed and sintered at 1280 degrees C for 1-32 h. The ...
Antiferromagnetism and heat capacity of NaCo2-xCuxO4 ceramics
(Elsevier Sci Ltd, Oxford, 2017)
Polycrystalline samples of NaCo2-xCuxO4 (x=0, 0.01, 0.03 and 0.05) were synthesized in two different ways: 1) by a mechanochemically assisted solid-state reaction method (MASSR) and 2) by a citric acid complex method (CAC). ...