TY  - JOUR
AU  - Stojmenović, M.
AU  - Bošković, Snežana B
AU  - Žunić, Milan
AU  - Babić, Biljana M.
AU  - Matović, Branko
AU  - Bajuk-Bogdanović, Danica
AU  - Mentus, S.
PY  - 2015
UR  - http://rimsi.imsi.bg.ac.rs/handle/123456789/872
AB  - A series of four different powders ceria doped Ce1-xErxO2-delta (0.05  lt = x  lt = 0.20) were synthesized by applying self-propagating reaction at room temperature (SPRT method). SPRT procedure is based on the self-propagating room temperature reaction between metal nitrates and sodium hydroxide, wherein the reaction is spontaneous and terminates extremely fast. The method is known to assure very precise stoichiometry of the final product in comparison with a tailored composition. XRPD, Raman spectroscopy, TEM and BET measurements were used to characterize the nanopowders at room temperature. It was shown that all obtained powders were single phase solid solutions with a fluorite-type crystal structure and all powder particles have nanometric size (about 3-4 nm). Densification was performed at 1550 degrees C, in an air atmosphere for 2 h. XRPD, SEM and complex impedance method measurements were carried out on sintered samples. Single phase form was evidenced for each sintered materials. The best value of conductivity at 700 degrees C amounted to 1.10 x 10(-2) Omega(-1) cm(-1) for Ce0.85Er0.O-3(2-delta) sample. Corresponding activation energies of conductivity amounted to 0.28 eV in the temperature range 500-700 degrees C.
PB  - Elsevier Science Sa, Lausanne
T2  - Materials Chemistry and Physics
T1  - Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC
EP  - 431
SP  - 422
VL  - 153
DO  - 10.1016/j.matchemphys.2015.01.036
ER  - 

@article{
author = "Stojmenović, M. and Bošković, Snežana B and Žunić, Milan and Babić, Biljana M. and Matović, Branko and Bajuk-Bogdanović, Danica and Mentus, S.",
year = "2015",
abstract = "A series of four different powders ceria doped Ce1-xErxO2-delta (0.05  lt = x  lt = 0.20) were synthesized by applying self-propagating reaction at room temperature (SPRT method). SPRT procedure is based on the self-propagating room temperature reaction between metal nitrates and sodium hydroxide, wherein the reaction is spontaneous and terminates extremely fast. The method is known to assure very precise stoichiometry of the final product in comparison with a tailored composition. XRPD, Raman spectroscopy, TEM and BET measurements were used to characterize the nanopowders at room temperature. It was shown that all obtained powders were single phase solid solutions with a fluorite-type crystal structure and all powder particles have nanometric size (about 3-4 nm). Densification was performed at 1550 degrees C, in an air atmosphere for 2 h. XRPD, SEM and complex impedance method measurements were carried out on sintered samples. Single phase form was evidenced for each sintered materials. The best value of conductivity at 700 degrees C amounted to 1.10 x 10(-2) Omega(-1) cm(-1) for Ce0.85Er0.O-3(2-delta) sample. Corresponding activation energies of conductivity amounted to 0.28 eV in the temperature range 500-700 degrees C.",
publisher = "Elsevier Science Sa, Lausanne",
journal = "Materials Chemistry and Physics",
title = "Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC",
pages = "431-422",
volume = "153",
doi = "10.1016/j.matchemphys.2015.01.036"
}

Stojmenović, M., Bošković, S. B., Žunić, M., Babić, B. M., Matović, B., Bajuk-Bogdanović, D.,& Mentus, S.. (2015). Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC. in Materials Chemistry and Physics
Elsevier Science Sa, Lausanne., 153, 422-431.
https://doi.org/10.1016/j.matchemphys.2015.01.036

Stojmenović M, Bošković SB, Žunić M, Babić BM, Matović B, Bajuk-Bogdanović D, Mentus S. Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC. in Materials Chemistry and Physics. 2015;153:422-431.
doi:10.1016/j.matchemphys.2015.01.036 .

Stojmenović, M., Bošković, Snežana B, Žunić, Milan, Babić, Biljana M., Matović, Branko, Bajuk-Bogdanović, Danica, Mentus, S., "Studies on structural, morphological and electrical properties of Ce1-xErxO2-delta (x=0.05-0.20) as solid electrolyte for IT - SOFC" in Materials Chemistry and Physics, 153 (2015):422-431,
https://doi.org/10.1016/j.matchemphys.2015.01.036 . .

TY  - JOUR
AU  - Prekajski, Marija
AU  - Stojmenović, M.
AU  - Radojković, Aleksandar
AU  - Branković, Goran
AU  - Oraon, H.
AU  - Subasri, R.
AU  - Matović, Branko
PY  - 2014
UR  - http://rimsi.imsi.bg.ac.rs/handle/123456789/804
AB  - Solid solution Ce1-xBixO2-delta nanopowders with the composition of x = 0.1-0.5 were synthesized by using Self Propagating Room Temperature procedure (SPRT). The results obtained by XRPD show that synthesized samples were single-phase solid solution at room temperature. Powders were densified by using Conventional (CS) and Microwave (MS) Sintering techniques at different temperatures, in an air atmosphere for 1 h. Scanning electron microscopy (SEM) and complex impedance method measurements were carried out on sintered samples. Maximum achieved density was for sample with Ce0.80Bi0.20O2-delta composition for both applied sintering techniques. The highest conductivity was obtained for the ceramic composition Ce0.80Bi0.20O2-delta sintered by microwave technique at 700 degrees C.
PB  - Elsevier Science Sa, Lausanne
T2  - Journal of Alloys and Compounds
T1  - Sintering and electrical properties of Ce1-xBixO2-delta solid solution
EP  - 568
SP  - 563
VL  - 617
DO  - 10.1016/j.jallcom.2014.08.090
ER  - 

@article{
author = "Prekajski, Marija and Stojmenović, M. and Radojković, Aleksandar and Branković, Goran and Oraon, H. and Subasri, R. and Matović, Branko",
year = "2014",
abstract = "Solid solution Ce1-xBixO2-delta nanopowders with the composition of x = 0.1-0.5 were synthesized by using Self Propagating Room Temperature procedure (SPRT). The results obtained by XRPD show that synthesized samples were single-phase solid solution at room temperature. Powders were densified by using Conventional (CS) and Microwave (MS) Sintering techniques at different temperatures, in an air atmosphere for 1 h. Scanning electron microscopy (SEM) and complex impedance method measurements were carried out on sintered samples. Maximum achieved density was for sample with Ce0.80Bi0.20O2-delta composition for both applied sintering techniques. The highest conductivity was obtained for the ceramic composition Ce0.80Bi0.20O2-delta sintered by microwave technique at 700 degrees C.",
publisher = "Elsevier Science Sa, Lausanne",
journal = "Journal of Alloys and Compounds",
title = "Sintering and electrical properties of Ce1-xBixO2-delta solid solution",
pages = "568-563",
volume = "617",
doi = "10.1016/j.jallcom.2014.08.090"
}

Prekajski, M., Stojmenović, M., Radojković, A., Branković, G., Oraon, H., Subasri, R.,& Matović, B.. (2014). Sintering and electrical properties of Ce1-xBixO2-delta solid solution. in Journal of Alloys and Compounds
Elsevier Science Sa, Lausanne., 617, 563-568.
https://doi.org/10.1016/j.jallcom.2014.08.090

Prekajski M, Stojmenović M, Radojković A, Branković G, Oraon H, Subasri R, Matović B. Sintering and electrical properties of Ce1-xBixO2-delta solid solution. in Journal of Alloys and Compounds. 2014;617:563-568.
doi:10.1016/j.jallcom.2014.08.090 .

Prekajski, Marija, Stojmenović, M., Radojković, Aleksandar, Branković, Goran, Oraon, H., Subasri, R., Matović, Branko, "Sintering and electrical properties of Ce1-xBixO2-delta solid solution" in Journal of Alloys and Compounds, 617 (2014):563-568,
https://doi.org/10.1016/j.jallcom.2014.08.090 . .