AB  - The morphology, phase and chemical composition of Ni-Co alloy powders electrodeposited from an ammonium sulfate-boric acid containing electrolyte with different ratio of Ni/Co ions were investigated. The ratios of NVCo ions were 1/1, 1/2 and 1/3. The morphology, chemical composition and phase composition of the electrodeposited alloy powders were investigated using AES, SEM, EDS and XRD analysis. Composition of the electrolyte, i.e. the ratio of Ni/Co concentrations was found to influence both, the alloy phase composition and the morphology of Ni-Co alloy powders. At the highest ratio of Ni/Co = 1/1 concentrations typical 2D fern-like dendritic particles were obtained. With a decrease of NVCo ions ratio among 2D fern-like dendrites, 3D dendrites and different agglomerates were obtained. X-ray diffraction studies showed that the alloy powders mainly consisted of the face-centered cubic alpha-nickel phase and hexagonal close-packed alpha-cobalt phase and minor proportions of face-centered cubic alpha-cobalt phase. The occurrence of the latter phase was observed only in the alloy powder with the higher cobalt concentration in electrolyte. The electrodeposition of Ni-Co powders occurred in an anomalous manner.
PB  - Elsevier Science Inc, New York
T2  - Materials Characterization
T1  - Morphology and composition of Ni-Co electrodeposited powders
EP  - 1179
IS  - 12
SP  - 1173
VL  - 62
DO  - 10.1016/j.matchar.2011.09.001
ER  - 

@article{
author = "Maksimović, Vesna M and Lačnjevac, Uroš and Stoiljković, Milovan M and Pavlović, Miomir G. and Jović, Vladimir D",
year = "2011",
abstract = "The morphology, phase and chemical composition of Ni-Co alloy powders electrodeposited from an ammonium sulfate-boric acid containing electrolyte with different ratio of Ni/Co ions were investigated. The ratios of NVCo ions were 1/1, 1/2 and 1/3. The morphology, chemical composition and phase composition of the electrodeposited alloy powders were investigated using AES, SEM, EDS and XRD analysis. Composition of the electrolyte, i.e. the ratio of Ni/Co concentrations was found to influence both, the alloy phase composition and the morphology of Ni-Co alloy powders. At the highest ratio of Ni/Co = 1/1 concentrations typical 2D fern-like dendritic particles were obtained. With a decrease of NVCo ions ratio among 2D fern-like dendrites, 3D dendrites and different agglomerates were obtained. X-ray diffraction studies showed that the alloy powders mainly consisted of the face-centered cubic alpha-nickel phase and hexagonal close-packed alpha-cobalt phase and minor proportions of face-centered cubic alpha-cobalt phase. The occurrence of the latter phase was observed only in the alloy powder with the higher cobalt concentration in electrolyte. The electrodeposition of Ni-Co powders occurred in an anomalous manner.",
publisher = "Elsevier Science Inc, New York",
journal = "Materials Characterization",
title = "Morphology and composition of Ni-Co electrodeposited powders",
pages = "1179-1173",
number = "12",
volume = "62",
doi = "10.1016/j.matchar.2011.09.001"
}

Maksimović, V. M., Lačnjevac, U., Stoiljković, M. M., Pavlović, M. G.,& Jović, V. D.. (2011). Morphology and composition of Ni-Co electrodeposited powders. in Materials Characterization
Elsevier Science Inc, New York., 62(12), 1173-1179.
https://doi.org/10.1016/j.matchar.2011.09.001

Maksimović VM, Lačnjevac U, Stoiljković MM, Pavlović MG, Jović VD. Morphology and composition of Ni-Co electrodeposited powders. in Materials Characterization. 2011;62(12):1173-1179.
doi:10.1016/j.matchar.2011.09.001 .

Maksimović, Vesna M, Lačnjevac, Uroš, Stoiljković, Milovan M, Pavlović, Miomir G., Jović, Vladimir D, "Morphology and composition of Ni-Co electrodeposited powders" in Materials Characterization, 62, no. 12 (2011):1173-1179,
https://doi.org/10.1016/j.matchar.2011.09.001 . .